C28000 Muntz Metal vs. Solder Alloy 701
C28000 Muntz Metal belongs to the copper alloys classification, while solder alloy 701 belongs to the otherwise unclassified metals. There are 22 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is C28000 Muntz Metal and the bottom bar is solder alloy 701.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 51 |
| Elongation at Break, % | 10 to 45 | |
| 37 |
| Poisson's Ratio | 0.31 | |
| 0.36 |
| Shear Modulus, GPa | 40 | |
| 19 |
| Tensile Strength: Ultimate (UTS), MPa | 330 to 610 | |
| 54 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 61 |
| Melting Completion (Liquidus), °C | 900 | |
| 230 |
| Melting Onset (Solidus), °C | 900 | |
| 220 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 220 |
| Thermal Conductivity, W/m-K | 120 | |
| 52 |
| Thermal Expansion, µm/m-K | 21 | |
| 22 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 28 | |
| 14 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 31 | |
| 17 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.0 | |
| 7.4 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 18 |
| Embodied Energy, MJ/kg | 46 | |
| 300 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.2 | |
| 3.8 |
| Stiffness to Weight: Bending, points | 20 | |
| 17 |
| Strength to Weight: Axial, points | 11 to 21 | |
| 2.0 |
| Strength to Weight: Bending, points | 13 to 20 | |
| 4.3 |
| Thermal Diffusivity, mm2/s | 40 | |
| 32 |
| Thermal Shock Resistance, points | 11 to 20 | |
| 3.5 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.0010 |
| Antimony (Sb), % | 0 | |
| 0 to 0.1 |
| Arsenic (As), % | 0 | |
| 0 to 0.030 |
| Bismuth (Bi), % | 0 | |
| 0 to 0.1 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0020 |
| Copper (Cu), % | 59 to 63 | |
| 0 to 0.050 |
| Gold (Au), % | 0 | |
| 0 to 0.050 |
| Indium (In), % | 0 | |
| 0 to 0.1 |
| Iron (Fe), % | 0 to 0.070 | |
| 0 to 0.020 |
| Lead (Pb), % | 0 to 0.3 | |
| 0 to 0.070 |
| Nickel (Ni), % | 0 | |
| 0 to 0.010 |
| Silver (Ag), % | 0 | |
| 3.5 to 3.9 |
| Tin (Sn), % | 0 | |
| 95.6 to 96.5 |
| Zinc (Zn), % | 36.3 to 41 | |
| 0 to 0.0010 |
| Residuals, % | 0 to 0.3 | |
| 0 |