C28000 Muntz Metal vs. C34500 Brass
Both C28000 Muntz Metal and C34500 brass are copper alloys. They have a very high 96% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is C28000 Muntz Metal and the bottom bar is C34500 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 100 |
| Elongation at Break, % | 10 to 45 | |
| 12 to 28 |
| Poisson's Ratio | 0.31 | |
| 0.31 |
| Shear Modulus, GPa | 40 | |
| 40 |
| Shear Strength, MPa | 230 to 330 | |
| 220 to 260 |
| Tensile Strength: Ultimate (UTS), MPa | 330 to 610 | |
| 340 to 430 |
| Tensile Strength: Yield (Proof), MPa | 150 to 370 | |
| 120 to 180 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 120 | |
| 120 |
| Melting Completion (Liquidus), °C | 900 | |
| 910 |
| Melting Onset (Solidus), °C | 900 | |
| 890 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 380 |
| Thermal Conductivity, W/m-K | 120 | |
| 120 |
| Thermal Expansion, µm/m-K | 21 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 28 | |
| 26 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 31 | |
| 29 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 23 | |
| 24 |
| Density, g/cm3 | 8.0 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 2.6 |
| Embodied Energy, MJ/kg | 46 | |
| 45 |
| Embodied Water, L/kg | 320 | |
| 320 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 27 to 240 | |
| 42 to 75 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 110 to 670 | |
| 69 to 160 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.1 |
| Stiffness to Weight: Bending, points | 20 | |
| 19 |
| Strength to Weight: Axial, points | 11 to 21 | |
| 12 to 15 |
| Strength to Weight: Bending, points | 13 to 20 | |
| 13 to 16 |
| Thermal Diffusivity, mm2/s | 40 | |
| 37 |
| Thermal Shock Resistance, points | 11 to 20 | |
| 11 to 14 |
Alloy Composition
| Copper (Cu), % | 59 to 63 | |
| 62 to 65 |
| Iron (Fe), % | 0 to 0.070 | |
| 0 to 0.15 |
| Lead (Pb), % | 0 to 0.3 | |
| 1.5 to 2.5 |
| Zinc (Zn), % | 36.3 to 41 | |
| 32 to 36.5 |
| Residuals, % | 0 | |
| 0 to 0.4 |