C28500 Muntz Metal vs. C27400 Brass

Both C28500 Muntz Metal and C27400 brass are copper alloys. They have a very high 96% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is C28500 Muntz Metal and the bottom bar is C27400 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 100
110
Poisson's Ratio 0.3
0.31
Rockwell B Hardness 150
53 to 91
Shear Modulus, GPa 40
40
Tensile Strength: Ultimate (UTS), MPa 520
370 to 650

Thermal Properties

Latent Heat of Fusion, J/g 170
170
Maximum Temperature: Mechanical, °C 110
120
Melting Completion (Liquidus), °C 900
920
Melting Onset (Solidus), °C 890
870
Specific Heat Capacity, J/kg-K 390
390
Thermal Conductivity, W/m-K 100
120
Thermal Expansion, µm/m-K 21
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 29
28
Electrical Conductivity: Equal Weight (Specific), % IACS 33
31

Otherwise Unclassified Properties

Base Metal Price, % relative 22
23
Density, g/cm3 7.9
8.0
Embodied Carbon, kg CO2/kg material 2.7
2.7
Embodied Energy, MJ/kg 46
45
Embodied Water, L/kg 320
320

Common Calculations

Stiffness to Weight: Axial, points 7.3
7.2
Stiffness to Weight: Bending, points 20
20
Strength to Weight: Axial, points 18
13 to 23
Strength to Weight: Bending, points 18
14 to 21
Thermal Diffusivity, mm2/s 33
37
Thermal Shock Resistance, points 17
12 to 22

Alloy Composition

Copper (Cu), % 57 to 59
61 to 64
Iron (Fe), % 0 to 0.35
0 to 0.1
Lead (Pb), % 0 to 0.25
0 to 0.050
Zinc (Zn), % 39.5 to 43
35.6 to 39
Residuals, % 0
0 to 0.3