C31400 Bronze vs. C70600 Copper-nickel
Both C31400 bronze and C70600 copper-nickel are copper alloys. They have 88% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is C31400 bronze and the bottom bar is C70600 copper-nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 120 |
| Elongation at Break, % | 6.8 to 29 | |
| 3.0 to 34 |
| Poisson's Ratio | 0.33 | |
| 0.34 |
| Shear Modulus, GPa | 42 | |
| 46 |
| Shear Strength, MPa | 180 to 240 | |
| 190 to 330 |
| Tensile Strength: Ultimate (UTS), MPa | 270 to 420 | |
| 290 to 570 |
| Tensile Strength: Yield (Proof), MPa | 78 to 310 | |
| 63 to 270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 200 | |
| 220 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 220 |
| Melting Completion (Liquidus), °C | 1040 | |
| 1150 |
| Melting Onset (Solidus), °C | 1010 | |
| 1100 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 390 |
| Thermal Conductivity, W/m-K | 180 | |
| 44 |
| Thermal Expansion, µm/m-K | 18 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 42 | |
| 9.8 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 43 | |
| 9.9 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 29 | |
| 33 |
| Density, g/cm3 | 8.8 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 3.4 |
| Embodied Energy, MJ/kg | 42 | |
| 51 |
| Embodied Water, L/kg | 310 | |
| 300 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 26 to 59 | |
| 6.5 to 160 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 28 to 420 | |
| 16 to 290 |
| Stiffness to Weight: Axial, points | 7.1 | |
| 7.7 |
| Stiffness to Weight: Bending, points | 18 | |
| 19 |
| Strength to Weight: Axial, points | 8.7 to 13 | |
| 9.1 to 18 |
| Strength to Weight: Bending, points | 11 to 14 | |
| 11 to 17 |
| Thermal Diffusivity, mm2/s | 54 | |
| 13 |
| Thermal Shock Resistance, points | 9.6 to 15 | |
| 9.8 to 19 |
Alloy Composition
| Copper (Cu), % | 87.5 to 90.5 | |
| 84.7 to 90 |
| Iron (Fe), % | 0 to 0.1 | |
| 1.0 to 1.8 |
| Lead (Pb), % | 1.3 to 2.5 | |
| 0 to 0.050 |
| Manganese (Mn), % | 0 | |
| 0 to 1.0 |
| Nickel (Ni), % | 0 to 0.7 | |
| 9.0 to 11 |
| Zinc (Zn), % | 5.8 to 11.2 | |
| 0 to 1.0 |
| Residuals, % | 0 | |
| 0 to 0.5 |