C32000 Brass vs. C61300 Bronze
Both C32000 brass and C61300 bronze are copper alloys. They have 85% of their average alloy composition in common.
For each property being compared, the top bar is C32000 brass and the bottom bar is C61300 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 110 |
| Elongation at Break, % | 6.8 to 29 | |
| 34 to 40 |
| Poisson's Ratio | 0.33 | |
| 0.34 |
| Shear Modulus, GPa | 41 | |
| 43 |
| Shear Strength, MPa | 180 to 280 | |
| 370 to 390 |
| Tensile Strength: Ultimate (UTS), MPa | 270 to 470 | |
| 550 to 580 |
| Tensile Strength: Yield (Proof), MPa | 78 to 390 | |
| 230 to 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 220 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 210 |
| Melting Completion (Liquidus), °C | 1020 | |
| 1050 |
| Melting Onset (Solidus), °C | 990 | |
| 1040 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 420 |
| Thermal Conductivity, W/m-K | 160 | |
| 55 |
| Thermal Expansion, µm/m-K | 19 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 36 | |
| 12 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 37 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 28 | |
| 29 |
| Density, g/cm3 | 8.7 | |
| 8.5 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 3.0 |
| Embodied Energy, MJ/kg | 42 | |
| 49 |
| Embodied Water, L/kg | 310 | |
| 370 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 30 to 59 | |
| 150 to 190 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 28 to 680 | |
| 230 to 410 |
| Stiffness to Weight: Axial, points | 7.1 | |
| 7.5 |
| Stiffness to Weight: Bending, points | 18 | |
| 19 |
| Strength to Weight: Axial, points | 8.8 to 15 | |
| 18 to 19 |
| Strength to Weight: Bending, points | 11 to 16 | |
| 18 |
| Thermal Diffusivity, mm2/s | 47 | |
| 15 |
| Thermal Shock Resistance, points | 9.5 to 16 | |
| 19 to 20 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 6.0 to 7.5 |
| Copper (Cu), % | 83.5 to 86.5 | |
| 88 to 91.8 |
| Iron (Fe), % | 0 to 0.1 | |
| 2.0 to 3.0 |
| Lead (Pb), % | 1.5 to 2.2 | |
| 0 to 0.010 |
| Manganese (Mn), % | 0 | |
| 0 to 0.2 |
| Nickel (Ni), % | 0 to 0.25 | |
| 0 to 0.15 |
| Phosphorus (P), % | 0 | |
| 0 to 0.015 |
| Silicon (Si), % | 0 | |
| 0 to 0.1 |
| Tin (Sn), % | 0 | |
| 0.2 to 0.5 |
| Zinc (Zn), % | 10.6 to 15 | |
| 0 to 0.2 |
| Residuals, % | 0 | |
| 0 to 0.2 |