C33200 Brass vs. ASTM B631 Class B

C33200 brass belongs to the copper alloys classification, while ASTM B631 class B belongs to the otherwise unclassified metals. There are 16 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is C33200 brass and the bottom bar is ASTM B631 class B.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 100
210
Poisson's Ratio 0.31
0.31
Shear Modulus, GPa 40
78 to 79

Thermal Properties

Latent Heat of Fusion, J/g 170
150
Melting Completion (Liquidus), °C 930
2460 to 2480
Specific Heat Capacity, J/kg-K 380
170
Thermal Conductivity, W/m-K 120
450
Thermal Expansion, µm/m-K 20
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 26
50 to 53
Electrical Conductivity: Equal Weight (Specific), % IACS 28
32 to 34

Otherwise Unclassified Properties

Density, g/cm3 8.2
14
Embodied Carbon, kg CO2/kg material 2.6
49
Embodied Energy, MJ/kg 44
760

Common Calculations

Stiffness to Weight: Axial, points 7.1
8.1
Stiffness to Weight: Bending, points 19
14
Thermal Diffusivity, mm2/s 37
190