C34200 Brass vs. 4045 Aluminum

C34200 brass belongs to the copper alloys classification, while 4045 aluminum belongs to the aluminum alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is C34200 brass and the bottom bar is 4045 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 100
71
Elongation at Break, % 3.0 to 17
2.3
Poisson's Ratio 0.31
0.33
Shear Modulus, GPa 40
27
Shear Strength, MPa 230 to 360
69
Tensile Strength: Ultimate (UTS), MPa 370 to 650
120
Tensile Strength: Yield (Proof), MPa 150 to 420
64

Thermal Properties

Latent Heat of Fusion, J/g 170
540
Maximum Temperature: Mechanical, °C 120
160
Melting Completion (Liquidus), °C 910
600
Melting Onset (Solidus), °C 890
580
Specific Heat Capacity, J/kg-K 380
900
Thermal Conductivity, W/m-K 120
170
Thermal Expansion, µm/m-K 21
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 26
45
Electrical Conductivity: Equal Weight (Specific), % IACS 29
160

Otherwise Unclassified Properties

Base Metal Price, % relative 24
9.5
Density, g/cm3 8.2
2.6
Embodied Carbon, kg CO2/kg material 2.6
7.8
Embodied Energy, MJ/kg 45
150
Embodied Water, L/kg 320
1070

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 9.0 to 98
2.4
Resilience: Unit (Modulus of Resilience), kJ/m3 110 to 870
29
Stiffness to Weight: Axial, points 7.1
15
Stiffness to Weight: Bending, points 19
54
Strength to Weight: Axial, points 13 to 22
13
Strength to Weight: Bending, points 14 to 20
21
Thermal Diffusivity, mm2/s 37
74
Thermal Shock Resistance, points 12 to 22
5.7

Alloy Composition

Aluminum (Al), % 0
87.4 to 91
Copper (Cu), % 62 to 65
0 to 0.3
Iron (Fe), % 0 to 0.1
0 to 0.8
Lead (Pb), % 1.5 to 2.5
0
Magnesium (Mg), % 0
0 to 0.050
Manganese (Mn), % 0
0 to 0.050
Silicon (Si), % 0
9.0 to 11
Titanium (Ti), % 0
0 to 0.2
Zinc (Zn), % 32 to 36.5
0 to 0.1
Residuals, % 0
0 to 0.15