C35600 Brass vs. CC753S Brass
Both C35600 brass and CC753S brass are copper alloys. They have a very high 97% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is C35600 brass and the bottom bar is CC753S brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 100 |
| Poisson's Ratio | 0.31 | |
| 0.31 |
| Shear Modulus, GPa | 39 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 340 to 650 | |
| 340 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 120 | |
| 120 |
| Melting Completion (Liquidus), °C | 900 | |
| 820 |
| Melting Onset (Solidus), °C | 890 | |
| 780 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 390 |
| Thermal Conductivity, W/m-K | 120 | |
| 99 |
| Thermal Expansion, µm/m-K | 21 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 26 | |
| 26 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 29 | |
| 29 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 23 | |
| 23 |
| Density, g/cm3 | 8.1 | |
| 8.1 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 2.8 |
| Embodied Energy, MJ/kg | 45 | |
| 47 |
| Embodied Water, L/kg | 320 | |
| 330 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.0 | |
| 7.1 |
| Stiffness to Weight: Bending, points | 19 | |
| 19 |
| Strength to Weight: Axial, points | 11 to 22 | |
| 12 |
| Strength to Weight: Bending, points | 13 to 21 | |
| 13 |
| Thermal Diffusivity, mm2/s | 38 | |
| 32 |
| Thermal Shock Resistance, points | 11 to 22 | |
| 11 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0.4 to 0.8 |
| Antimony (Sb), % | 0 | |
| 0 to 0.050 |
| Copper (Cu), % | 60 to 63 | |
| 56.8 to 60.5 |
| Iron (Fe), % | 0 to 0.1 | |
| 0.5 to 0.8 |
| Lead (Pb), % | 2.0 to 3.0 | |
| 1.8 to 2.5 |
| Manganese (Mn), % | 0 | |
| 0 to 0.2 |
| Nickel (Ni), % | 0 | |
| 0.5 to 1.2 |
| Phosphorus (P), % | 0 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 | |
| 0 to 0.050 |
| Tin (Sn), % | 0 | |
| 0 to 0.8 |
| Zinc (Zn), % | 33.4 to 38 | |
| 33.1 to 40 |
| Residuals, % | 0 to 0.5 | |
| 0 |