C35600 Brass vs. C54400 Bronze
Both C35600 brass and C54400 bronze are copper alloys. They have 67% of their average alloy composition in common.
For each property being compared, the top bar is C35600 brass and the bottom bar is C54400 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 110 |
| Poisson's Ratio | 0.31 | |
| 0.34 |
| Rockwell B Hardness | 53 to 91 | |
| 67 to 93 |
| Rockwell Superficial 30T Hardness | 52 to 78 | |
| 33 to 79 |
| Shear Modulus, GPa | 39 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 340 to 650 | |
| 330 to 720 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 190 |
| Maximum Temperature: Mechanical, °C | 120 | |
| 170 |
| Melting Completion (Liquidus), °C | 900 | |
| 1000 |
| Melting Onset (Solidus), °C | 890 | |
| 930 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 370 |
| Thermal Conductivity, W/m-K | 120 | |
| 86 |
| Thermal Expansion, µm/m-K | 21 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 26 | |
| 19 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 29 | |
| 19 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 23 | |
| 31 |
| Density, g/cm3 | 8.1 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 2.9 |
| Embodied Energy, MJ/kg | 45 | |
| 48 |
| Embodied Water, L/kg | 320 | |
| 340 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.0 | |
| 6.8 |
| Stiffness to Weight: Bending, points | 19 | |
| 18 |
| Strength to Weight: Axial, points | 11 to 22 | |
| 10 to 22 |
| Strength to Weight: Bending, points | 13 to 21 | |
| 12 to 20 |
| Thermal Diffusivity, mm2/s | 38 | |
| 26 |
| Thermal Shock Resistance, points | 11 to 22 | |
| 12 to 26 |
Alloy Composition
| Copper (Cu), % | 60 to 63 | |
| 85.4 to 91.5 |
| Iron (Fe), % | 0 to 0.1 | |
| 0 to 0.1 |
| Lead (Pb), % | 2.0 to 3.0 | |
| 3.5 to 4.5 |
| Phosphorus (P), % | 0 | |
| 0.010 to 0.5 |
| Tin (Sn), % | 0 | |
| 3.5 to 4.5 |
| Zinc (Zn), % | 33.4 to 38 | |
| 1.5 to 4.5 |
| Residuals, % | 0 | |
| 0 to 0.5 |