C35600 Brass vs. R30012 Cobalt
C35600 brass belongs to the copper alloys classification, while R30012 cobalt belongs to the cobalt alloys. There are 22 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is C35600 brass and the bottom bar is R30012 cobalt.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 220 |
| Poisson's Ratio | 0.31 | |
| 0.28 |
| Shear Modulus, GPa | 39 | |
| 86 |
| Tensile Strength: Ultimate (UTS), MPa | 340 to 650 | |
| 830 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 320 |
| Melting Completion (Liquidus), °C | 900 | |
| 1470 |
| Melting Onset (Solidus), °C | 890 | |
| 1280 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 440 |
| Thermal Conductivity, W/m-K | 120 | |
| 15 |
| Thermal Expansion, µm/m-K | 21 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 26 | |
| 1.8 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 29 | |
| 1.8 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.1 | |
| 8.8 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 8.3 |
| Embodied Energy, MJ/kg | 45 | |
| 120 |
| Embodied Water, L/kg | 320 | |
| 480 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.0 | |
| 14 |
| Stiffness to Weight: Bending, points | 19 | |
| 23 |
| Strength to Weight: Axial, points | 11 to 22 | |
| 26 |
| Strength to Weight: Bending, points | 13 to 21 | |
| 22 |
| Thermal Diffusivity, mm2/s | 38 | |
| 3.8 |
| Thermal Shock Resistance, points | 11 to 22 | |
| 23 |
Alloy Composition
| Carbon (C), % | 0 | |
| 1.4 to 2.0 |
| Chromium (Cr), % | 0 | |
| 27 to 32 |
| Cobalt (Co), % | 0 | |
| 47.5 to 64.1 |
| Copper (Cu), % | 60 to 63 | |
| 0 |
| Iron (Fe), % | 0 to 0.1 | |
| 0 to 3.0 |
| Lead (Pb), % | 2.0 to 3.0 | |
| 0 |
| Molybdenum (Mo), % | 0 | |
| 0 to 1.0 |
| Nickel (Ni), % | 0 | |
| 0 to 3.0 |
| Silicon (Si), % | 0 | |
| 0 to 2.0 |
| Tungsten (W), % | 0 | |
| 7.5 to 9.5 |
| Zinc (Zn), % | 33.4 to 38 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |