C36200 Brass vs. 88-silver 12-tin-oxide
C36200 brass belongs to the copper alloys classification, while 88-silver 12-tin-oxide belongs to the otherwise unclassified metals. There are 6 material properties with values for both materials. Properties with values for just one material (24, in this case) are not shown.
For each property being compared, the top bar is C36200 brass and the bottom bar is 88-silver 12-tin-oxide.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 26 | |
| 84 to 86 |
| Elongation at Break, % | 20 to 53 | |
| 9.0 to 37 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 74 to 140 | |
| 24 to 70 |
| Shear Strength, MPa | 210 to 240 | |
| 150 to 160 |
| Tensile Strength: Ultimate (UTS), MPa | 340 to 420 | |
| 230 to 280 |
| Tensile Strength: Yield (Proof), MPa | 130 to 360 | |
| 110 to 260 |