C36200 Brass vs. CR015A Copper
Both C36200 brass and CR015A copper are copper alloys. They have 62% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is C36200 brass and the bottom bar is CR015A copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 120 |
| Elongation at Break, % | 20 to 53 | |
| 15 |
| Poisson's Ratio | 0.31 | |
| 0.34 |
| Shear Modulus, GPa | 39 | |
| 43 |
| Tensile Strength: Ultimate (UTS), MPa | 340 to 420 | |
| 220 |
| Tensile Strength: Yield (Proof), MPa | 130 to 360 | |
| 130 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 120 | |
| 200 |
| Melting Completion (Liquidus), °C | 900 | |
| 1090 |
| Melting Onset (Solidus), °C | 890 | |
| 1040 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 390 |
| Thermal Conductivity, W/m-K | 120 | |
| 390 |
| Thermal Expansion, µm/m-K | 21 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 26 | |
| 98 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 28 | |
| 99 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 23 | |
| 33 |
| Density, g/cm3 | 8.2 | |
| 9.0 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 2.7 |
| Embodied Energy, MJ/kg | 45 | |
| 42 |
| Embodied Water, L/kg | 320 | |
| 360 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 74 to 140 | |
| 29 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 89 to 630 | |
| 76 |
| Stiffness to Weight: Axial, points | 6.9 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 19 | |
| 18 |
| Strength to Weight: Axial, points | 11 to 14 | |
| 6.8 |
| Strength to Weight: Bending, points | 13 to 15 | |
| 9.0 |
| Thermal Diffusivity, mm2/s | 37 | |
| 110 |
| Thermal Shock Resistance, points | 11 to 14 | |
| 7.8 |
Alloy Composition
| Bismuth (Bi), % | 0 | |
| 0 to 0.00050 |
| Copper (Cu), % | 60 to 63 | |
| 99.883 to 99.939 |
| Iron (Fe), % | 0 to 0.15 | |
| 0 |
| Lead (Pb), % | 3.5 to 4.5 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0.0010 to 0.0070 |
| Silver (Ag), % | 0 | |
| 0.060 to 0.080 |
| Zinc (Zn), % | 32.4 to 36.5 | |
| 0 |