C36500 Muntz Metal vs. Nickel 689
C36500 Muntz Metal belongs to the copper alloys classification, while nickel 689 belongs to the nickel alloys. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is C36500 Muntz Metal and the bottom bar is nickel 689.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 210 |
| Elongation at Break, % | 40 | |
| 23 |
| Poisson's Ratio | 0.3 | |
| 0.29 |
| Shear Modulus, GPa | 39 | |
| 80 |
| Shear Strength, MPa | 270 | |
| 790 |
| Tensile Strength: Ultimate (UTS), MPa | 400 | |
| 1250 |
| Tensile Strength: Yield (Proof), MPa | 160 | |
| 690 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 330 |
| Maximum Temperature: Mechanical, °C | 120 | |
| 990 |
| Melting Completion (Liquidus), °C | 900 | |
| 1440 |
| Melting Onset (Solidus), °C | 890 | |
| 1390 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 450 |
| Thermal Expansion, µm/m-K | 21 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 23 | |
| 70 |
| Density, g/cm3 | 8.0 | |
| 8.5 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 11 |
| Embodied Energy, MJ/kg | 46 | |
| 150 |
| Embodied Water, L/kg | 320 | |
| 330 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 130 | |
| 240 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 120 | |
| 1170 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 14 |
| Stiffness to Weight: Bending, points | 20 | |
| 23 |
| Strength to Weight: Axial, points | 14 | |
| 41 |
| Strength to Weight: Bending, points | 15 | |
| 30 |
| Thermal Shock Resistance, points | 13 | |
| 35 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0.75 to 1.3 |
| Boron (B), % | 0 | |
| 0.0030 to 0.010 |
| Carbon (C), % | 0 | |
| 0.1 to 0.2 |
| Chromium (Cr), % | 0 | |
| 18 to 20 |
| Cobalt (Co), % | 0 | |
| 9.0 to 11 |
| Copper (Cu), % | 58 to 61 | |
| 0 |
| Iron (Fe), % | 0 to 0.15 | |
| 0 to 5.0 |
| Lead (Pb), % | 0.25 to 0.7 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0 to 0.5 |
| Molybdenum (Mo), % | 0 | |
| 9.0 to 10.5 |
| Nickel (Ni), % | 0 | |
| 48.3 to 60.9 |
| Phosphorus (P), % | 0 | |
| 0 to 0.015 |
| Silicon (Si), % | 0 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 | |
| 0 to 0.015 |
| Tin (Sn), % | 0 to 0.25 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 2.3 to 2.8 |
| Zinc (Zn), % | 37.5 to 41.8 | |
| 0 |
| Residuals, % | 0 to 0.4 | |
| 0 |