C36500 Muntz Metal vs. C18100 Copper
Both C36500 Muntz Metal and C18100 copper are copper alloys. They have 60% of their average alloy composition in common.
For each property being compared, the top bar is C36500 Muntz Metal and the bottom bar is C18100 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 120 |
| Elongation at Break, % | 40 | |
| 8.3 |
| Poisson's Ratio | 0.3 | |
| 0.34 |
| Rockwell B Hardness | 45 | |
| 80 |
| Shear Modulus, GPa | 39 | |
| 47 |
| Shear Strength, MPa | 270 | |
| 300 |
| Tensile Strength: Ultimate (UTS), MPa | 400 | |
| 510 |
| Tensile Strength: Yield (Proof), MPa | 160 | |
| 460 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 120 | |
| 200 |
| Melting Completion (Liquidus), °C | 900 | |
| 1080 |
| Melting Onset (Solidus), °C | 890 | |
| 1020 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 390 |
| Thermal Conductivity, W/m-K | 120 | |
| 320 |
| Thermal Expansion, µm/m-K | 21 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 28 | |
| 80 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 32 | |
| 81 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 23 | |
| 31 |
| Density, g/cm3 | 8.0 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 2.7 |
| Embodied Energy, MJ/kg | 46 | |
| 43 |
| Embodied Water, L/kg | 320 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 130 | |
| 40 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 120 | |
| 900 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.3 |
| Stiffness to Weight: Bending, points | 20 | |
| 18 |
| Strength to Weight: Axial, points | 14 | |
| 16 |
| Strength to Weight: Bending, points | 15 | |
| 16 |
| Thermal Diffusivity, mm2/s | 40 | |
| 94 |
| Thermal Shock Resistance, points | 13 | |
| 18 |
Alloy Composition
| Chromium (Cr), % | 0 | |
| 0.4 to 1.2 |
| Copper (Cu), % | 58 to 61 | |
| 98.7 to 99.49 |
| Iron (Fe), % | 0 to 0.15 | |
| 0 |
| Lead (Pb), % | 0.25 to 0.7 | |
| 0 |
| Magnesium (Mg), % | 0 | |
| 0.030 to 0.060 |
| Tin (Sn), % | 0 to 0.25 | |
| 0 |
| Zinc (Zn), % | 37.5 to 41.8 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 0.080 to 0.2 |
| Residuals, % | 0 | |
| 0 to 0.5 |