C38000 Brass vs. ASTM A182 Grade F24

C38000 brass belongs to the copper alloys classification, while ASTM A182 grade F24 belongs to the iron alloys. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is C38000 brass and the bottom bar is ASTM A182 grade F24.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 100
190
Elongation at Break, % 17
23
Poisson's Ratio 0.31
0.29
Shear Modulus, GPa 39
74
Shear Strength, MPa 230
420
Tensile Strength: Ultimate (UTS), MPa 380
670
Tensile Strength: Yield (Proof), MPa 120
460

Thermal Properties

Latent Heat of Fusion, J/g 170
260
Maximum Temperature: Mechanical, °C 110
460
Melting Completion (Liquidus), °C 800
1470
Melting Onset (Solidus), °C 760
1430
Specific Heat Capacity, J/kg-K 380
470
Thermal Conductivity, W/m-K 110
39
Thermal Expansion, µm/m-K 21
13

Otherwise Unclassified Properties

Base Metal Price, % relative 22
4.0
Density, g/cm3 8.0
7.8
Embodied Carbon, kg CO2/kg material 2.7
2.3
Embodied Energy, MJ/kg 46
33
Embodied Water, L/kg 330
61

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 50
140
Resilience: Unit (Modulus of Resilience), kJ/m3 74
570
Stiffness to Weight: Axial, points 7.1
13
Stiffness to Weight: Bending, points 19
24
Strength to Weight: Axial, points 13
24
Strength to Weight: Bending, points 14
22
Thermal Diffusivity, mm2/s 37
11
Thermal Shock Resistance, points 13
19

Alloy Composition

Aluminum (Al), % 0 to 0.5
0 to 0.020
Boron (B), % 0
0.0015 to 0.0070
Carbon (C), % 0
0.050 to 0.1
Chromium (Cr), % 0
2.2 to 2.6
Copper (Cu), % 55 to 60
0
Iron (Fe), % 0 to 0.35
94.5 to 96.1
Lead (Pb), % 1.5 to 2.5
0
Manganese (Mn), % 0
0.3 to 0.7
Molybdenum (Mo), % 0
0.9 to 1.1
Nitrogen (N), % 0
0 to 0.12
Phosphorus (P), % 0
0 to 0.020
Silicon (Si), % 0
0.15 to 0.45
Sulfur (S), % 0
0 to 0.010
Tin (Sn), % 0 to 0.3
0
Titanium (Ti), % 0
0.060 to 0.1
Vanadium (V), % 0
0.2 to 0.3
Zinc (Zn), % 35.9 to 43.5
0
Residuals, % 0 to 0.5
0