C40500 Penny Bronze vs. CC495K Bronze
Both C40500 penny bronze and CC495K bronze are copper alloys. They have 81% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is C40500 penny bronze and the bottom bar is CC495K bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 100 |
| Elongation at Break, % | 3.0 to 49 | |
| 7.0 |
| Poisson's Ratio | 0.34 | |
| 0.35 |
| Shear Modulus, GPa | 43 | |
| 37 |
| Tensile Strength: Ultimate (UTS), MPa | 270 to 540 | |
| 240 |
| Tensile Strength: Yield (Proof), MPa | 79 to 520 | |
| 120 |
Thermal Properties
| Latent Heat of Fusion, J/g | 200 | |
| 180 |
| Maximum Temperature: Mechanical, °C | 190 | |
| 140 |
| Melting Completion (Liquidus), °C | 1060 | |
| 930 |
| Melting Onset (Solidus), °C | 1020 | |
| 820 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 350 |
| Thermal Conductivity, W/m-K | 160 | |
| 48 |
| Thermal Expansion, µm/m-K | 18 | |
| 19 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 41 | |
| 10 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 42 | |
| 10 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 30 | |
| 33 |
| Density, g/cm3 | 8.8 | |
| 9.0 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 3.6 |
| Embodied Energy, MJ/kg | 43 | |
| 58 |
| Embodied Water, L/kg | 320 | |
| 400 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 16 to 110 | |
| 14 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 28 to 1200 | |
| 68 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 6.2 |
| Stiffness to Weight: Bending, points | 18 | |
| 17 |
| Strength to Weight: Axial, points | 8.5 to 17 | |
| 7.3 |
| Strength to Weight: Bending, points | 10 to 17 | |
| 9.4 |
| Thermal Diffusivity, mm2/s | 48 | |
| 15 |
| Thermal Shock Resistance, points | 9.5 to 19 | |
| 8.8 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.010 |
| Antimony (Sb), % | 0 | |
| 0 to 0.5 |
| Copper (Cu), % | 94 to 96 | |
| 76 to 82 |
| Iron (Fe), % | 0 to 0.050 | |
| 0 to 0.25 |
| Lead (Pb), % | 0 to 0.050 | |
| 8.0 to 11 |
| Manganese (Mn), % | 0 | |
| 0 to 0.2 |
| Nickel (Ni), % | 0 | |
| 0 to 2.0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.1 |
| Silicon (Si), % | 0 | |
| 0 to 0.010 |
| Sulfur (S), % | 0 | |
| 0 to 0.1 |
| Tin (Sn), % | 0.7 to 1.3 | |
| 9.0 to 11 |
| Zinc (Zn), % | 2.1 to 5.3 | |
| 0 to 2.0 |
| Residuals, % | 0 to 0.5 | |
| 0 |