C40500 Penny Bronze vs. Grade 28 Titanium
C40500 penny bronze belongs to the copper alloys classification, while grade 28 titanium belongs to the titanium alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is C40500 penny bronze and the bottom bar is grade 28 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 110 |
| Elongation at Break, % | 3.0 to 49 | |
| 11 to 17 |
| Poisson's Ratio | 0.34 | |
| 0.32 |
| Shear Modulus, GPa | 43 | |
| 40 |
| Shear Strength, MPa | 210 to 310 | |
| 420 to 590 |
| Tensile Strength: Ultimate (UTS), MPa | 270 to 540 | |
| 690 to 980 |
| Tensile Strength: Yield (Proof), MPa | 79 to 520 | |
| 540 to 810 |
Thermal Properties
| Latent Heat of Fusion, J/g | 200 | |
| 410 |
| Maximum Temperature: Mechanical, °C | 190 | |
| 330 |
| Melting Completion (Liquidus), °C | 1060 | |
| 1640 |
| Melting Onset (Solidus), °C | 1020 | |
| 1590 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 550 |
| Thermal Conductivity, W/m-K | 160 | |
| 8.3 |
| Thermal Expansion, µm/m-K | 18 | |
| 9.9 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 41 | |
| 1.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 42 | |
| 2.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 30 | |
| 36 |
| Density, g/cm3 | 8.8 | |
| 4.5 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 37 |
| Embodied Energy, MJ/kg | 43 | |
| 600 |
| Embodied Water, L/kg | 320 | |
| 370 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 16 to 110 | |
| 87 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 28 to 1200 | |
| 1370 to 3100 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 13 |
| Stiffness to Weight: Bending, points | 18 | |
| 35 |
| Strength to Weight: Axial, points | 8.5 to 17 | |
| 43 to 61 |
| Strength to Weight: Bending, points | 10 to 17 | |
| 39 to 49 |
| Thermal Diffusivity, mm2/s | 48 | |
| 3.4 |
| Thermal Shock Resistance, points | 9.5 to 19 | |
| 47 to 66 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 2.5 to 3.5 |
| Carbon (C), % | 0 | |
| 0 to 0.080 |
| Copper (Cu), % | 94 to 96 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.015 |
| Iron (Fe), % | 0 to 0.050 | |
| 0 to 0.25 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.030 |
| Oxygen (O), % | 0 | |
| 0 to 0.15 |
| Ruthenium (Ru), % | 0 | |
| 0.080 to 0.14 |
| Tin (Sn), % | 0.7 to 1.3 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 92.4 to 95.4 |
| Vanadium (V), % | 0 | |
| 2.0 to 3.0 |
| Zinc (Zn), % | 2.1 to 5.3 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.4 |