C42200 Brass vs. AWS BVPd-1
C42200 brass belongs to the copper alloys classification, while AWS BVPd-1 belongs to the otherwise unclassified metals. There are 15 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.
For each property being compared, the top bar is C42200 brass and the bottom bar is AWS BVPd-1.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 150 |
| Poisson's Ratio | 0.33 | |
| 0.37 |
| Shear Modulus, GPa | 42 | |
| 56 |
| Tensile Strength: Ultimate (UTS), MPa | 300 to 610 | |
| 240 |
Thermal Properties
| Latent Heat of Fusion, J/g | 200 | |
| 200 |
| Melting Completion (Liquidus), °C | 1040 | |
| 1240 |
| Melting Onset (Solidus), °C | 1020 | |
| 1230 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 310 |
| Thermal Expansion, µm/m-K | 18 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.6 | |
| 11 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.7 |
| Stiffness to Weight: Bending, points | 19 | |
| 16 |
| Strength to Weight: Axial, points | 9.5 to 19 | |
| 6.1 |
| Strength to Weight: Bending, points | 11 to 18 | |
| 7.9 |
| Thermal Shock Resistance, points | 10 to 21 | |
| 9.8 |
Alloy Composition
| Cadmium (Cd), % | 0 | |
| 0 to 0.0010 |
| Carbon (C), % | 0 | |
| 0 to 0.0050 |
| Cobalt (Co), % | 0 | |
| 33.9 to 36 |
| Copper (Cu), % | 86 to 89 | |
| 0 |
| Iron (Fe), % | 0 to 0.050 | |
| 0 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 to 0.0020 |
| Nickel (Ni), % | 0 | |
| 0 to 0.060 |
| Palladium (Pd), % | 0 | |
| 64 to 66 |
| Phosphorus (P), % | 0 to 0.35 | |
| 0 to 0.0020 |
| Tin (Sn), % | 0.8 to 1.4 | |
| 0 |
| Zinc (Zn), % | 8.7 to 13.2 | |
| 0 to 0.0010 |
| Residuals, % | 0 to 0.5 | |
| 0 |