C42200 Brass vs. SAE-AISI 1038 Steel
C42200 brass belongs to the copper alloys classification, while SAE-AISI 1038 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is C42200 brass and the bottom bar is SAE-AISI 1038 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 190 |
| Elongation at Break, % | 2.0 to 46 | |
| 14 to 20 |
| Poisson's Ratio | 0.33 | |
| 0.29 |
| Shear Modulus, GPa | 42 | |
| 73 |
| Shear Strength, MPa | 210 to 350 | |
| 370 to 390 |
| Tensile Strength: Ultimate (UTS), MPa | 300 to 610 | |
| 590 to 640 |
| Tensile Strength: Yield (Proof), MPa | 100 to 570 | |
| 320 to 540 |
Thermal Properties
| Latent Heat of Fusion, J/g | 200 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 400 |
| Melting Completion (Liquidus), °C | 1040 | |
| 1460 |
| Melting Onset (Solidus), °C | 1020 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 470 |
| Thermal Conductivity, W/m-K | 130 | |
| 51 |
| Thermal Expansion, µm/m-K | 18 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 31 | |
| 7.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 32 | |
| 8.0 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 29 | |
| 1.8 |
| Density, g/cm3 | 8.6 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 1.4 |
| Embodied Energy, MJ/kg | 44 | |
| 18 |
| Embodied Water, L/kg | 320 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 12 to 110 | |
| 83 to 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 49 to 1460 | |
| 270 to 790 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 13 |
| Stiffness to Weight: Bending, points | 19 | |
| 24 |
| Strength to Weight: Axial, points | 9.5 to 19 | |
| 21 to 23 |
| Strength to Weight: Bending, points | 11 to 18 | |
| 20 to 21 |
| Thermal Diffusivity, mm2/s | 39 | |
| 14 |
| Thermal Shock Resistance, points | 10 to 21 | |
| 19 to 20 |
Alloy Composition
| Carbon (C), % | 0 | |
| 0.35 to 0.42 |
| Copper (Cu), % | 86 to 89 | |
| 0 |
| Iron (Fe), % | 0 to 0.050 | |
| 98.6 to 99.05 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0.6 to 0.9 |
| Phosphorus (P), % | 0 to 0.35 | |
| 0 to 0.040 |
| Sulfur (S), % | 0 | |
| 0 to 0.050 |
| Tin (Sn), % | 0.8 to 1.4 | |
| 0 |
| Zinc (Zn), % | 8.7 to 13.2 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |