C42500 Brass vs. EN 1.5503 Steel
C42500 brass belongs to the copper alloys classification, while EN 1.5503 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is C42500 brass and the bottom bar is EN 1.5503 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 190 |
| Elongation at Break, % | 2.0 to 49 | |
| 12 to 17 |
| Poisson's Ratio | 0.33 | |
| 0.29 |
| Shear Modulus, GPa | 42 | |
| 73 |
| Shear Strength, MPa | 220 to 360 | |
| 270 to 320 |
| Tensile Strength: Ultimate (UTS), MPa | 310 to 630 | |
| 400 to 520 |
| Tensile Strength: Yield (Proof), MPa | 120 to 590 | |
| 270 to 430 |
Thermal Properties
| Latent Heat of Fusion, J/g | 200 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 400 |
| Melting Completion (Liquidus), °C | 1030 | |
| 1460 |
| Melting Onset (Solidus), °C | 1010 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 470 |
| Thermal Conductivity, W/m-K | 120 | |
| 52 |
| Thermal Expansion, µm/m-K | 18 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 28 | |
| 7.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 29 | |
| 8.1 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 30 | |
| 1.8 |
| Density, g/cm3 | 8.7 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 1.4 |
| Embodied Energy, MJ/kg | 46 | |
| 18 |
| Embodied Water, L/kg | 330 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 12 to 130 | |
| 41 to 81 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 64 to 1570 | |
| 200 to 490 |
| Stiffness to Weight: Axial, points | 7.1 | |
| 13 |
| Stiffness to Weight: Bending, points | 18 | |
| 24 |
| Strength to Weight: Axial, points | 9.9 to 20 | |
| 14 to 19 |
| Strength to Weight: Bending, points | 12 to 19 | |
| 15 to 18 |
| Thermal Diffusivity, mm2/s | 36 | |
| 14 |
| Thermal Shock Resistance, points | 11 to 22 | |
| 12 to 15 |
Alloy Composition
| Boron (B), % | 0 | |
| 0.00080 to 0.0050 |
| Carbon (C), % | 0 | |
| 0.16 to 0.2 |
| Copper (Cu), % | 87 to 90 | |
| 0 to 0.25 |
| Iron (Fe), % | 0 to 0.050 | |
| 98.4 to 99.239 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0.6 to 0.8 |
| Phosphorus (P), % | 0 to 0.35 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 | |
| 0 to 0.3 |
| Sulfur (S), % | 0 | |
| 0 to 0.025 |
| Tin (Sn), % | 1.5 to 3.0 | |
| 0 |
| Zinc (Zn), % | 6.1 to 11.5 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |