C42600 Brass vs. AWS ENiCrMo-4
C42600 brass belongs to the copper alloys classification, while AWS ENiCrMo-4 belongs to the nickel alloys. There are 20 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is C42600 brass and the bottom bar is AWS ENiCrMo-4.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 220 |
| Elongation at Break, % | 1.1 to 40 | |
| 28 |
| Poisson's Ratio | 0.33 | |
| 0.29 |
| Shear Modulus, GPa | 42 | |
| 84 |
| Tensile Strength: Ultimate (UTS), MPa | 410 to 830 | |
| 790 |
Thermal Properties
| Latent Heat of Fusion, J/g | 200 | |
| 320 |
| Melting Completion (Liquidus), °C | 1030 | |
| 1590 |
| Melting Onset (Solidus), °C | 1010 | |
| 1530 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 410 |
| Thermal Expansion, µm/m-K | 18 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 70 |
| Density, g/cm3 | 8.7 | |
| 9.0 |
| Embodied Carbon, kg CO2/kg material | 2.9 | |
| 13 |
| Embodied Energy, MJ/kg | 48 | |
| 170 |
| Embodied Water, L/kg | 340 | |
| 280 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.1 | |
| 13 |
| Stiffness to Weight: Bending, points | 18 | |
| 22 |
| Strength to Weight: Axial, points | 13 to 27 | |
| 24 |
| Strength to Weight: Bending, points | 14 to 23 | |
| 21 |
| Thermal Shock Resistance, points | 15 to 29 | |
| 22 |
Alloy Composition
| Carbon (C), % | 0 | |
| 0 to 0.020 |
| Chromium (Cr), % | 0 | |
| 14.5 to 16.5 |
| Cobalt (Co), % | 0 | |
| 0 to 2.5 |
| Copper (Cu), % | 87 to 90 | |
| 0 to 0.5 |
| Iron (Fe), % | 0.050 to 0.2 | |
| 4.0 to 7.0 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 15 to 17 |
| Nickel (Ni), % | 0.050 to 0.2 | |
| 49.9 to 63.5 |
| Phosphorus (P), % | 0.020 to 0.050 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 | |
| 0 to 0.2 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Tin (Sn), % | 2.5 to 4.0 | |
| 0 |
| Tungsten (W), % | 0 | |
| 3.0 to 4.5 |
| Vanadium (V), % | 0 | |
| 0 to 0.35 |
| Zinc (Zn), % | 5.3 to 10.4 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.5 |