C42600 Brass vs. EN 2.4889 Nickel
C42600 brass belongs to the copper alloys classification, while EN 2.4889 nickel belongs to the nickel alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is C42600 brass and the bottom bar is EN 2.4889 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 200 |
| Elongation at Break, % | 1.1 to 40 | |
| 39 |
| Poisson's Ratio | 0.33 | |
| 0.28 |
| Shear Modulus, GPa | 42 | |
| 77 |
| Shear Strength, MPa | 280 to 470 | |
| 490 |
| Tensile Strength: Ultimate (UTS), MPa | 410 to 830 | |
| 720 |
| Tensile Strength: Yield (Proof), MPa | 220 to 810 | |
| 270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 200 | |
| 350 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 1200 |
| Melting Completion (Liquidus), °C | 1030 | |
| 1350 |
| Melting Onset (Solidus), °C | 1010 | |
| 1300 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 480 |
| Thermal Conductivity, W/m-K | 110 | |
| 13 |
| Thermal Expansion, µm/m-K | 18 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 25 | |
| 1.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 26 | |
| 1.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 42 |
| Density, g/cm3 | 8.7 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 2.9 | |
| 6.9 |
| Embodied Energy, MJ/kg | 48 | |
| 98 |
| Embodied Water, L/kg | 340 | |
| 250 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 9.4 to 140 | |
| 220 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 230 to 2970 | |
| 180 |
| Stiffness to Weight: Axial, points | 7.1 | |
| 14 |
| Stiffness to Weight: Bending, points | 18 | |
| 24 |
| Strength to Weight: Axial, points | 13 to 27 | |
| 25 |
| Strength to Weight: Bending, points | 14 to 23 | |
| 22 |
| Thermal Diffusivity, mm2/s | 33 | |
| 3.4 |
| Thermal Shock Resistance, points | 15 to 29 | |
| 19 |
Alloy Composition
| Carbon (C), % | 0 | |
| 0.050 to 0.12 |
| Cerium (Ce), % | 0 | |
| 0.030 to 0.090 |
| Chromium (Cr), % | 0 | |
| 26 to 29 |
| Copper (Cu), % | 87 to 90 | |
| 0 to 0.3 |
| Iron (Fe), % | 0.050 to 0.2 | |
| 21 to 25 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0 to 1.0 |
| Nickel (Ni), % | 0.050 to 0.2 | |
| 45 to 50.4 |
| Phosphorus (P), % | 0.020 to 0.050 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 | |
| 2.5 to 3.0 |
| Sulfur (S), % | 0 | |
| 0 to 0.010 |
| Tin (Sn), % | 2.5 to 4.0 | |
| 0 |
| Zinc (Zn), % | 5.3 to 10.4 | |
| 0 |
| Residuals, % | 0 to 0.2 | |
| 0 |