C43400 Brass vs. C86800 Bronze
Both C43400 brass and C86800 bronze are copper alloys. They have 70% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is C43400 brass and the bottom bar is C86800 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 110 |
| Elongation at Break, % | 3.0 to 49 | |
| 22 |
| Poisson's Ratio | 0.33 | |
| 0.31 |
| Shear Modulus, GPa | 42 | |
| 42 |
| Tensile Strength: Ultimate (UTS), MPa | 310 to 690 | |
| 570 |
| Tensile Strength: Yield (Proof), MPa | 110 to 560 | |
| 260 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 180 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 140 |
| Melting Completion (Liquidus), °C | 1020 | |
| 900 |
| Melting Onset (Solidus), °C | 990 | |
| 880 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 400 |
| Thermal Expansion, µm/m-K | 19 | |
| 20 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 31 | |
| 9.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 32 | |
| 10 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 28 | |
| 24 |
| Density, g/cm3 | 8.6 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 3.0 |
| Embodied Energy, MJ/kg | 44 | |
| 51 |
| Embodied Water, L/kg | 320 | |
| 320 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 19 to 120 | |
| 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 57 to 1420 | |
| 310 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.7 |
| Stiffness to Weight: Bending, points | 19 | |
| 20 |
| Strength to Weight: Axial, points | 10 to 22 | |
| 20 |
| Strength to Weight: Bending, points | 12 to 20 | |
| 19 |
| Thermal Shock Resistance, points | 11 to 24 | |
| 18 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 2.0 |
| Copper (Cu), % | 84 to 87 | |
| 53.5 to 57 |
| Iron (Fe), % | 0 to 0.050 | |
| 1.0 to 2.5 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 to 0.2 |
| Manganese (Mn), % | 0 | |
| 2.5 to 4.0 |
| Nickel (Ni), % | 0 | |
| 2.5 to 4.0 |
| Tin (Sn), % | 0.4 to 1.0 | |
| 0 to 1.0 |
| Zinc (Zn), % | 11.4 to 15.6 | |
| 28.3 to 40.5 |
| Residuals, % | 0 | |
| 0 to 1.0 |