C46400 Brass vs. EN 1.7272 Steel
C46400 brass belongs to the copper alloys classification, while EN 1.7272 steel belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is C46400 brass and the bottom bar is EN 1.7272 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 190 |
| Poisson's Ratio | 0.31 | |
| 0.29 |
| Shear Modulus, GPa | 40 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 400 to 500 | |
| 490 to 1650 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 120 | |
| 410 |
| Melting Completion (Liquidus), °C | 900 | |
| 1460 |
| Melting Onset (Solidus), °C | 890 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 470 |
| Thermal Conductivity, W/m-K | 120 | |
| 45 |
| Thermal Expansion, µm/m-K | 21 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 26 | |
| 7.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 29 | |
| 8.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 23 | |
| 2.2 |
| Density, g/cm3 | 8.0 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 1.5 |
| Embodied Energy, MJ/kg | 47 | |
| 19 |
| Embodied Water, L/kg | 330 | |
| 49 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.2 | |
| 13 |
| Stiffness to Weight: Bending, points | 20 | |
| 24 |
| Strength to Weight: Axial, points | 14 to 17 | |
| 17 to 59 |
| Strength to Weight: Bending, points | 15 to 17 | |
| 18 to 40 |
| Thermal Diffusivity, mm2/s | 38 | |
| 12 |
| Thermal Shock Resistance, points | 13 to 16 | |
| 14 to 48 |
Alloy Composition
| Boron (B), % | 0 | |
| 0.00080 to 0.0050 |
| Carbon (C), % | 0 | |
| 0.28 to 0.33 |
| Chromium (Cr), % | 0 | |
| 0.4 to 0.55 |
| Copper (Cu), % | 59 to 62 | |
| 0 to 0.25 |
| Iron (Fe), % | 0 to 0.1 | |
| 97.2 to 98.3 |
| Lead (Pb), % | 0 to 0.2 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0.9 to 1.2 |
| Molybdenum (Mo), % | 0 | |
| 0.1 to 0.15 |
| Phosphorus (P), % | 0 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 | |
| 0 to 0.3 |
| Sulfur (S), % | 0 | |
| 0 to 0.025 |
| Tin (Sn), % | 0.5 to 1.0 | |
| 0 |
| Zinc (Zn), % | 36.3 to 40.5 | |
| 0 |
| Residuals, % | 0 to 0.4 | |
| 0 |