C46400 Brass vs. EN 1.8959 Steel
C46400 brass belongs to the copper alloys classification, while EN 1.8959 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is C46400 brass and the bottom bar is EN 1.8959 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 190 |
| Elongation at Break, % | 17 to 40 | |
| 16 |
| Poisson's Ratio | 0.31 | |
| 0.29 |
| Shear Modulus, GPa | 40 | |
| 73 |
| Shear Strength, MPa | 270 to 310 | |
| 350 |
| Tensile Strength: Ultimate (UTS), MPa | 400 to 500 | |
| 570 |
| Tensile Strength: Yield (Proof), MPa | 160 to 320 | |
| 340 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 120 | |
| 420 |
| Melting Completion (Liquidus), °C | 900 | |
| 1460 |
| Melting Onset (Solidus), °C | 890 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 470 |
| Thermal Conductivity, W/m-K | 120 | |
| 39 |
| Thermal Expansion, µm/m-K | 21 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 26 | |
| 7.6 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 29 | |
| 8.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 23 | |
| 2.7 |
| Density, g/cm3 | 8.0 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 1.6 |
| Embodied Energy, MJ/kg | 47 | |
| 21 |
| Embodied Water, L/kg | 330 | |
| 52 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 76 to 140 | |
| 78 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 120 to 500 | |
| 300 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 13 |
| Stiffness to Weight: Bending, points | 20 | |
| 24 |
| Strength to Weight: Axial, points | 14 to 17 | |
| 20 |
| Strength to Weight: Bending, points | 15 to 17 | |
| 19 |
| Thermal Diffusivity, mm2/s | 38 | |
| 10 |
| Thermal Shock Resistance, points | 13 to 16 | |
| 17 |
Alloy Composition
| Carbon (C), % | 0 | |
| 0 to 0.19 |
| Chromium (Cr), % | 0 | |
| 0.35 to 0.85 |
| Copper (Cu), % | 59 to 62 | |
| 0.2 to 0.6 |
| Iron (Fe), % | 0 to 0.1 | |
| 94.9 to 99 |
| Lead (Pb), % | 0 to 0.2 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0.45 to 1.6 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.35 |
| Nickel (Ni), % | 0 | |
| 0 to 0.7 |
| Nitrogen (N), % | 0 | |
| 0 to 0.010 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 | |
| 0 to 0.55 |
| Sulfur (S), % | 0 | |
| 0 to 0.040 |
| Tin (Sn), % | 0.5 to 1.0 | |
| 0 |
| Zinc (Zn), % | 36.3 to 40.5 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 0 to 0.17 |
| Residuals, % | 0 to 0.4 | |
| 0 |