C46500 Brass vs. Grade 704C Zirconium
C46500 brass belongs to the copper alloys classification, while grade 704C zirconium belongs to the otherwise unclassified metals. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is C46500 brass and the bottom bar is grade 704C zirconium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 97 |
| Elongation at Break, % | 18 to 50 | |
| 11 |
| Poisson's Ratio | 0.31 | |
| 0.34 |
| Rockwell B Hardness | 55 to 95 | |
| 85 |
| Shear Modulus, GPa | 40 | |
| 36 |
| Tensile Strength: Ultimate (UTS), MPa | 380 to 610 | |
| 470 |
| Tensile Strength: Yield (Proof), MPa | 190 to 490 | |
| 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 240 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 270 |
| Thermal Conductivity, W/m-K | 120 | |
| 21 |
| Thermal Expansion, µm/m-K | 21 | |
| 5.9 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.0 | |
| 6.7 |
| Embodied Water, L/kg | 330 | |
| 460 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 99 to 160 | |
| 48 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 170 to 1170 | |
| 490 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 8.1 |
| Stiffness to Weight: Bending, points | 20 | |
| 23 |
| Strength to Weight: Axial, points | 13 to 21 | |
| 20 |
| Strength to Weight: Bending, points | 15 to 20 | |
| 20 |
| Thermal Diffusivity, mm2/s | 38 | |
| 12 |
| Thermal Shock Resistance, points | 13 to 20 | |
| 58 |
Alloy Composition
| Arsenic (As), % | 0.020 to 0.060 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.1 |
| Copper (Cu), % | 59 to 62 | |
| 0 |
| Hafnium (Hf), % | 0 | |
| 0 to 4.5 |
| Hydrogen (H), % | 0 | |
| 0 to 0.0050 |
| Iron (Fe), % | 0 to 0.1 | |
| 0 to 0.3 |
| Lead (Pb), % | 0 to 0.2 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.030 |
| Oxygen (O), % | 0 | |
| 0 to 0.3 |
| Phosphorus (P), % | 0 | |
| 0 to 0.010 |
| Tin (Sn), % | 0.5 to 1.0 | |
| 1.0 to 2.0 |
| Zinc (Zn), % | 36.2 to 40.5 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 92.9 to 99 |
| Residuals, % | 0 to 0.4 | |
| 0 |