C46500 Brass vs. C17510 Copper
Both C46500 brass and C17510 copper are copper alloys. They have 61% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is C46500 brass and the bottom bar is C17510 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 120 |
| Elongation at Break, % | 18 to 50 | |
| 5.4 to 37 |
| Poisson's Ratio | 0.31 | |
| 0.34 |
| Rockwell B Hardness | 55 to 95 | |
| 44 to 99 |
| Shear Modulus, GPa | 40 | |
| 44 |
| Shear Strength, MPa | 280 to 380 | |
| 210 to 500 |
| Tensile Strength: Ultimate (UTS), MPa | 380 to 610 | |
| 310 to 860 |
| Tensile Strength: Yield (Proof), MPa | 190 to 490 | |
| 120 to 750 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 220 |
| Maximum Temperature: Mechanical, °C | 120 | |
| 220 |
| Melting Completion (Liquidus), °C | 900 | |
| 1070 |
| Melting Onset (Solidus), °C | 890 | |
| 1030 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 390 |
| Thermal Conductivity, W/m-K | 120 | |
| 210 |
| Thermal Expansion, µm/m-K | 21 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 26 | |
| 22 to 54 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 29 | |
| 23 to 54 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 23 | |
| 49 |
| Density, g/cm3 | 8.0 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 4.2 |
| Embodied Energy, MJ/kg | 47 | |
| 65 |
| Embodied Water, L/kg | 330 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 99 to 160 | |
| 39 to 92 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 170 to 1170 | |
| 64 to 2410 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.4 |
| Stiffness to Weight: Bending, points | 20 | |
| 18 |
| Strength to Weight: Axial, points | 13 to 21 | |
| 9.7 to 27 |
| Strength to Weight: Bending, points | 15 to 20 | |
| 11 to 23 |
| Thermal Diffusivity, mm2/s | 38 | |
| 60 |
| Thermal Shock Resistance, points | 13 to 20 | |
| 11 to 30 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.2 |
| Arsenic (As), % | 0.020 to 0.060 | |
| 0 |
| Beryllium (Be), % | 0 | |
| 0.2 to 0.6 |
| Cobalt (Co), % | 0 | |
| 0 to 0.3 |
| Copper (Cu), % | 59 to 62 | |
| 95.9 to 98.4 |
| Iron (Fe), % | 0 to 0.1 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 to 0.2 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 1.4 to 2.2 |
| Silicon (Si), % | 0 | |
| 0 to 0.2 |
| Tin (Sn), % | 0.5 to 1.0 | |
| 0 |
| Zinc (Zn), % | 36.2 to 40.5 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.5 |