C47940 Brass vs. Nickel 601

C47940 brass belongs to the copper alloys classification, while nickel 601 belongs to the nickel alloys. There are 27 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is C47940 brass and the bottom bar is nickel 601.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 100
200
Elongation at Break, % 14 to 34
10 to 38
Poisson's Ratio 0.31
0.28
Shear Modulus, GPa 40
76
Shear Strength, MPa 250 to 310
440 to 530
Tensile Strength: Ultimate (UTS), MPa 380 to 520
660 to 890
Tensile Strength: Yield (Proof), MPa 160 to 390
290 to 800

Thermal Properties

Latent Heat of Fusion, J/g 170
320
Maximum Temperature: Mechanical, °C 130
1100
Melting Completion (Liquidus), °C 850
1410
Melting Onset (Solidus), °C 800
1360
Specific Heat Capacity, J/kg-K 380
470
Thermal Conductivity, W/m-K 110
11
Thermal Expansion, µm/m-K 20
14

Otherwise Unclassified Properties

Base Metal Price, % relative 25
49
Density, g/cm3 8.2
8.3
Embodied Carbon, kg CO2/kg material 2.8
8.0
Embodied Energy, MJ/kg 47
110
Embodied Water, L/kg 330
280

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 68 to 100
86 to 200
Resilience: Unit (Modulus of Resilience), kJ/m3 120 to 740
210 to 1630
Stiffness to Weight: Axial, points 7.1
13
Stiffness to Weight: Bending, points 19
23
Strength to Weight: Axial, points 13 to 17
22 to 30
Strength to Weight: Bending, points 14 to 17
20 to 25
Thermal Diffusivity, mm2/s 36
2.8
Thermal Shock Resistance, points 13 to 17
17 to 23

Alloy Composition

Aluminum (Al), % 0
1.0 to 1.7
Carbon (C), % 0
0 to 0.1
Chromium (Cr), % 0
21 to 25
Copper (Cu), % 63 to 66
0 to 1.0
Iron (Fe), % 0.1 to 1.0
7.7 to 20
Lead (Pb), % 1.0 to 2.0
0
Manganese (Mn), % 0
0 to 1.0
Nickel (Ni), % 0.1 to 0.5
58 to 63
Silicon (Si), % 0
0 to 0.5
Sulfur (S), % 0
0 to 0.015
Tin (Sn), % 1.2 to 2.0
0
Zinc (Zn), % 28.1 to 34.6
0
Residuals, % 0 to 0.4
0