C47940 Brass vs. C90200 Bronze
Both C47940 brass and C90200 bronze are copper alloys. They have 67% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is C47940 brass and the bottom bar is C90200 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 110 |
| Elongation at Break, % | 14 to 34 | |
| 30 |
| Poisson's Ratio | 0.31 | |
| 0.34 |
| Shear Modulus, GPa | 40 | |
| 41 |
| Tensile Strength: Ultimate (UTS), MPa | 380 to 520 | |
| 260 |
| Tensile Strength: Yield (Proof), MPa | 160 to 390 | |
| 110 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 200 |
| Maximum Temperature: Mechanical, °C | 130 | |
| 180 |
| Melting Completion (Liquidus), °C | 850 | |
| 1050 |
| Melting Onset (Solidus), °C | 800 | |
| 880 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 370 |
| Thermal Conductivity, W/m-K | 110 | |
| 62 |
| Thermal Expansion, µm/m-K | 20 | |
| 18 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 25 | |
| 34 |
| Density, g/cm3 | 8.2 | |
| 8.8 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 3.3 |
| Embodied Energy, MJ/kg | 47 | |
| 53 |
| Embodied Water, L/kg | 330 | |
| 370 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 68 to 100 | |
| 63 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 120 to 740 | |
| 55 |
| Stiffness to Weight: Axial, points | 7.1 | |
| 7.0 |
| Stiffness to Weight: Bending, points | 19 | |
| 18 |
| Strength to Weight: Axial, points | 13 to 17 | |
| 8.3 |
| Strength to Weight: Bending, points | 14 to 17 | |
| 10 |
| Thermal Diffusivity, mm2/s | 36 | |
| 19 |
| Thermal Shock Resistance, points | 13 to 17 | |
| 9.5 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.0050 |
| Antimony (Sb), % | 0 | |
| 0 to 0.2 |
| Copper (Cu), % | 63 to 66 | |
| 91 to 94 |
| Iron (Fe), % | 0.1 to 1.0 | |
| 0 to 0.2 |
| Lead (Pb), % | 1.0 to 2.0 | |
| 0 to 0.3 |
| Nickel (Ni), % | 0.1 to 0.5 | |
| 0 to 0.5 |
| Phosphorus (P), % | 0 | |
| 0 to 0.050 |
| Silicon (Si), % | 0 | |
| 0 to 0.0050 |
| Sulfur (S), % | 0 | |
| 0 to 0.050 |
| Tin (Sn), % | 1.2 to 2.0 | |
| 6.0 to 8.0 |
| Zinc (Zn), % | 28.1 to 34.6 | |
| 0 to 0.5 |
| Residuals, % | 0 | |
| 0 to 0.6 |