C48200 Brass vs. C68000 Brass
Both C48200 brass and C68000 brass are copper alloys. They have a very high 97% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is C48200 brass and the bottom bar is C68000 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 100 |
| Elongation at Break, % | 15 to 40 | |
| 27 |
| Poisson's Ratio | 0.31 | |
| 0.3 |
| Shear Modulus, GPa | 40 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 400 to 500 | |
| 390 |
| Tensile Strength: Yield (Proof), MPa | 160 to 320 | |
| 140 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 120 | |
| 120 |
| Melting Completion (Liquidus), °C | 900 | |
| 880 |
| Melting Onset (Solidus), °C | 890 | |
| 870 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 390 |
| Thermal Conductivity, W/m-K | 120 | |
| 96 |
| Thermal Expansion, µm/m-K | 21 | |
| 21 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 23 | |
| 23 |
| Density, g/cm3 | 8.0 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 2.8 |
| Embodied Energy, MJ/kg | 47 | |
| 48 |
| Embodied Water, L/kg | 330 | |
| 330 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 61 to 140 | |
| 82 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 120 to 500 | |
| 95 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.3 |
| Stiffness to Weight: Bending, points | 19 | |
| 20 |
| Strength to Weight: Axial, points | 14 to 17 | |
| 14 |
| Strength to Weight: Bending, points | 15 to 17 | |
| 15 |
| Thermal Diffusivity, mm2/s | 38 | |
| 31 |
| Thermal Shock Resistance, points | 13 to 16 | |
| 13 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.010 |
| Copper (Cu), % | 59 to 62 | |
| 56 to 60 |
| Iron (Fe), % | 0 to 0.1 | |
| 0.25 to 1.3 |
| Lead (Pb), % | 0.4 to 1.0 | |
| 0 to 0.050 |
| Manganese (Mn), % | 0 | |
| 0.010 to 0.5 |
| Nickel (Ni), % | 0 | |
| 0.2 to 0.8 |
| Silicon (Si), % | 0 | |
| 0.040 to 0.15 |
| Tin (Sn), % | 0.5 to 1.0 | |
| 0.75 to 1.1 |
| Zinc (Zn), % | 35.5 to 40.1 | |
| 35.6 to 42.8 |
| Residuals, % | 0 | |
| 0 to 0.5 |