C48600 Brass vs. EN 1.0038 Steel
C48600 brass belongs to the copper alloys classification, while EN 1.0038 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is C48600 brass and the bottom bar is EN 1.0038 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 190 |
| Elongation at Break, % | 20 to 25 | |
| 23 to 25 |
| Poisson's Ratio | 0.31 | |
| 0.29 |
| Shear Modulus, GPa | 39 | |
| 73 |
| Shear Strength, MPa | 180 to 230 | |
| 240 to 270 |
| Tensile Strength: Ultimate (UTS), MPa | 280 to 360 | |
| 380 to 430 |
| Tensile Strength: Yield (Proof), MPa | 110 to 170 | |
| 200 to 220 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 120 | |
| 400 |
| Melting Completion (Liquidus), °C | 900 | |
| 1460 |
| Melting Onset (Solidus), °C | 890 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 470 |
| Thermal Conductivity, W/m-K | 110 | |
| 49 |
| Thermal Expansion, µm/m-K | 21 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 25 | |
| 7.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 28 | |
| 8.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 24 | |
| 2.1 |
| Density, g/cm3 | 8.1 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 1.4 |
| Embodied Energy, MJ/kg | 47 | |
| 19 |
| Embodied Water, L/kg | 330 | |
| 48 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 55 to 59 | |
| 72 to 88 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 61 to 140 | |
| 110 to 130 |
| Stiffness to Weight: Axial, points | 7.1 | |
| 13 |
| Stiffness to Weight: Bending, points | 19 | |
| 24 |
| Strength to Weight: Axial, points | 9.5 to 12 | |
| 13 to 15 |
| Strength to Weight: Bending, points | 12 to 14 | |
| 15 to 16 |
| Thermal Diffusivity, mm2/s | 36 | |
| 13 |
| Thermal Shock Resistance, points | 9.3 to 12 | |
| 12 to 13 |
Alloy Composition
| Arsenic (As), % | 0.020 to 0.25 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.23 |
| Chromium (Cr), % | 0 | |
| 0 to 0.3 |
| Copper (Cu), % | 59 to 62 | |
| 0 to 0.6 |
| Iron (Fe), % | 0 | |
| 97.1 to 100 |
| Lead (Pb), % | 1.0 to 2.5 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0 to 1.5 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.080 |
| Nickel (Ni), % | 0 | |
| 0 to 0.3 |
| Nitrogen (N), % | 0 | |
| 0 to 0.014 |
| Phosphorus (P), % | 0 | |
| 0 to 0.045 |
| Silicon (Si), % | 0 | |
| 0 to 0.55 |
| Sulfur (S), % | 0 | |
| 0 to 0.045 |
| Tin (Sn), % | 0.3 to 1.5 | |
| 0 |
| Zinc (Zn), % | 33.4 to 39.7 | |
| 0 |
| Residuals, % | 0 to 0.4 | |
| 0 |