C48600 Brass vs. C10800 Copper
Both C48600 brass and C10800 copper are copper alloys. They have 61% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is C48600 brass and the bottom bar is C10800 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 120 |
| Elongation at Break, % | 20 to 25 | |
| 4.0 to 50 |
| Poisson's Ratio | 0.31 | |
| 0.34 |
| Rockwell B Hardness | 55 to 58 | |
| 10 to 60 |
| Shear Modulus, GPa | 39 | |
| 43 |
| Shear Strength, MPa | 180 to 230 | |
| 150 to 200 |
| Tensile Strength: Ultimate (UTS), MPa | 280 to 360 | |
| 220 to 380 |
| Tensile Strength: Yield (Proof), MPa | 110 to 170 | |
| 75 to 370 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 120 | |
| 200 |
| Melting Completion (Liquidus), °C | 900 | |
| 1080 |
| Melting Onset (Solidus), °C | 890 | |
| 1080 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 390 |
| Thermal Conductivity, W/m-K | 110 | |
| 350 |
| Thermal Expansion, µm/m-K | 21 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 25 | |
| 92 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 28 | |
| 92 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 24 | |
| 31 |
| Density, g/cm3 | 8.1 | |
| 9.0 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 2.6 |
| Embodied Energy, MJ/kg | 47 | |
| 41 |
| Embodied Water, L/kg | 330 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 55 to 59 | |
| 15 to 88 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 61 to 140 | |
| 24 to 600 |
| Stiffness to Weight: Axial, points | 7.1 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 19 | |
| 18 |
| Strength to Weight: Axial, points | 9.5 to 12 | |
| 6.8 to 12 |
| Strength to Weight: Bending, points | 12 to 14 | |
| 9.1 to 13 |
| Thermal Diffusivity, mm2/s | 36 | |
| 100 |
| Thermal Shock Resistance, points | 9.3 to 12 | |
| 7.8 to 13 |
Alloy Composition
| Arsenic (As), % | 0.020 to 0.25 | |
| 0 |
| Copper (Cu), % | 59 to 62 | |
| 99.95 to 99.995 |
| Lead (Pb), % | 1.0 to 2.5 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0.0050 to 0.012 |
| Tin (Sn), % | 0.3 to 1.5 | |
| 0 |
| Zinc (Zn), % | 33.4 to 39.7 | |
| 0 |
| Residuals, % | 0 to 0.4 | |
| 0 |