C48600 Brass vs. C63800 Bronze
Both C48600 brass and C63800 bronze are copper alloys. They have 61% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is C48600 brass and the bottom bar is C63800 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 110 |
| Elongation at Break, % | 20 to 25 | |
| 7.9 to 41 |
| Poisson's Ratio | 0.31 | |
| 0.34 |
| Rockwell B Hardness | 55 to 58 | |
| 94 to 110 |
| Shear Modulus, GPa | 39 | |
| 43 |
| Shear Strength, MPa | 180 to 230 | |
| 320 to 500 |
| Tensile Strength: Ultimate (UTS), MPa | 280 to 360 | |
| 460 to 1010 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 240 |
| Maximum Temperature: Mechanical, °C | 120 | |
| 200 |
| Melting Completion (Liquidus), °C | 900 | |
| 1030 |
| Melting Onset (Solidus), °C | 890 | |
| 1000 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 410 |
| Thermal Conductivity, W/m-K | 110 | |
| 40 |
| Thermal Expansion, µm/m-K | 21 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 25 | |
| 10 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 28 | |
| 10 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 24 | |
| 30 |
| Density, g/cm3 | 8.1 | |
| 8.6 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 2.8 |
| Embodied Energy, MJ/kg | 47 | |
| 45 |
| Embodied Water, L/kg | 330 | |
| 330 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.1 | |
| 7.4 |
| Stiffness to Weight: Bending, points | 19 | |
| 19 |
| Strength to Weight: Axial, points | 9.5 to 12 | |
| 15 to 33 |
| Strength to Weight: Bending, points | 12 to 14 | |
| 15 to 26 |
| Thermal Diffusivity, mm2/s | 36 | |
| 11 |
| Thermal Shock Resistance, points | 9.3 to 12 | |
| 17 to 36 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 2.5 to 3.1 |
| Arsenic (As), % | 0.020 to 0.25 | |
| 0 |
| Cobalt (Co), % | 0 | |
| 0.25 to 0.55 |
| Copper (Cu), % | 59 to 62 | |
| 92.4 to 95.8 |
| Iron (Fe), % | 0 | |
| 0 to 0.2 |
| Lead (Pb), % | 1.0 to 2.5 | |
| 0 to 0.050 |
| Manganese (Mn), % | 0 | |
| 0 to 0.1 |
| Nickel (Ni), % | 0 | |
| 0 to 0.2 |
| Silicon (Si), % | 0 | |
| 1.5 to 2.1 |
| Tin (Sn), % | 0.3 to 1.5 | |
| 0 |
| Zinc (Zn), % | 33.4 to 39.7 | |
| 0 to 0.8 |
| Residuals, % | 0 | |
| 0 to 0.5 |