C48600 Brass vs. C67600 Bronze
Both C48600 brass and C67600 bronze are copper alloys. They have a very high 97% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is C48600 brass and the bottom bar is C67600 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 100 |
| Elongation at Break, % | 20 to 25 | |
| 13 to 33 |
| Poisson's Ratio | 0.31 | |
| 0.31 |
| Shear Modulus, GPa | 39 | |
| 40 |
| Shear Strength, MPa | 180 to 230 | |
| 270 to 350 |
| Tensile Strength: Ultimate (UTS), MPa | 280 to 360 | |
| 430 to 570 |
| Tensile Strength: Yield (Proof), MPa | 110 to 170 | |
| 170 to 380 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 120 | |
| 120 |
| Melting Completion (Liquidus), °C | 900 | |
| 890 |
| Melting Onset (Solidus), °C | 890 | |
| 870 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 380 |
| Thermal Conductivity, W/m-K | 110 | |
| 110 |
| Thermal Expansion, µm/m-K | 21 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 25 | |
| 24 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 28 | |
| 27 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 24 | |
| 23 |
| Density, g/cm3 | 8.1 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 2.8 |
| Embodied Energy, MJ/kg | 47 | |
| 47 |
| Embodied Water, L/kg | 330 | |
| 330 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 55 to 59 | |
| 63 to 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 61 to 140 | |
| 140 to 680 |
| Stiffness to Weight: Axial, points | 7.1 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 19 | |
| 20 |
| Strength to Weight: Axial, points | 9.5 to 12 | |
| 15 to 20 |
| Strength to Weight: Bending, points | 12 to 14 | |
| 16 to 19 |
| Thermal Diffusivity, mm2/s | 36 | |
| 35 |
| Thermal Shock Resistance, points | 9.3 to 12 | |
| 14 to 19 |
Alloy Composition
| Arsenic (As), % | 0.020 to 0.25 | |
| 0 |
| Copper (Cu), % | 59 to 62 | |
| 57 to 60 |
| Iron (Fe), % | 0 | |
| 0.4 to 1.3 |
| Lead (Pb), % | 1.0 to 2.5 | |
| 0.5 to 1.0 |
| Manganese (Mn), % | 0 | |
| 0.050 to 0.5 |
| Tin (Sn), % | 0.3 to 1.5 | |
| 0.5 to 1.5 |
| Zinc (Zn), % | 33.4 to 39.7 | |
| 35.2 to 41.6 |
| Residuals, % | 0 | |
| 0 to 0.5 |