C49300 Brass vs. AWS BAg-26

C49300 brass belongs to the copper alloys classification, while AWS BAg-26 belongs to the otherwise unclassified metals. They have 72% of their average alloy composition in common. There are 17 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is C49300 brass and the bottom bar is AWS BAg-26.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 100
98
Poisson's Ratio 0.31
0.32
Shear Modulus, GPa 40
37
Tensile Strength: Ultimate (UTS), MPa 430 to 520
160

Thermal Properties

Latent Heat of Fusion, J/g 170
160
Melting Completion (Liquidus), °C 880
800
Melting Onset (Solidus), °C 840
710
Specific Heat Capacity, J/kg-K 380
350
Thermal Expansion, µm/m-K 20
21

Otherwise Unclassified Properties

Density, g/cm3 8.0
8.5
Embodied Carbon, kg CO2/kg material 3.0
26
Embodied Energy, MJ/kg 50
410

Common Calculations

Stiffness to Weight: Axial, points 7.2
6.4
Stiffness to Weight: Bending, points 19
18
Strength to Weight: Axial, points 15 to 18
5.2
Strength to Weight: Bending, points 16 to 18
7.7
Thermal Shock Resistance, points 14 to 18
5.6

Alloy Composition

Aluminum (Al), % 0 to 0.5
0
Antimony (Sb), % 0 to 0.5
0
Bismuth (Bi), % 0.5 to 2.0
0
Copper (Cu), % 58 to 62
37 to 39
Iron (Fe), % 0 to 0.1
0
Lead (Pb), % 0 to 0.010
0
Manganese (Mn), % 0 to 0.030
1.5 to 2.5
Nickel (Ni), % 0 to 1.5
1.5 to 2.5
Phosphorus (P), % 0 to 0.2
0
Selenium (Se), % 0 to 0.2
0
Silicon (Si), % 0 to 0.1
0
Silver (Ag), % 0
24 to 26
Tin (Sn), % 1.0 to 1.8
0
Zinc (Zn), % 30.6 to 40.5
31 to 35
Residuals, % 0
0 to 0.15