C49300 Brass vs. Austempered Cast Iron
C49300 brass belongs to the copper alloys classification, while austempered cast iron belongs to the iron alloys. There are 25 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is C49300 brass and the bottom bar is austempered cast iron.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 180 |
| Elongation at Break, % | 4.5 to 20 | |
| 1.1 to 13 |
| Poisson's Ratio | 0.31 | |
| 0.29 |
| Shear Modulus, GPa | 40 | |
| 62 to 69 |
| Tensile Strength: Ultimate (UTS), MPa | 430 to 520 | |
| 860 to 1800 |
| Tensile Strength: Yield (Proof), MPa | 210 to 410 | |
| 560 to 1460 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 280 |
| Melting Completion (Liquidus), °C | 880 | |
| 1380 |
| Melting Onset (Solidus), °C | 840 | |
| 1340 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 490 |
| Thermal Conductivity, W/m-K | 88 | |
| 42 |
| Thermal Expansion, µm/m-K | 20 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 26 | |
| 2.9 |
| Density, g/cm3 | 8.0 | |
| 7.5 |
| Embodied Carbon, kg CO2/kg material | 3.0 | |
| 1.8 |
| Embodied Energy, MJ/kg | 50 | |
| 25 |
| Embodied Water, L/kg | 370 | |
| 48 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 21 to 71 | |
| 19 to 95 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 220 to 800 | |
| 880 to 3970 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 13 |
| Stiffness to Weight: Bending, points | 19 | |
| 25 |
| Strength to Weight: Axial, points | 15 to 18 | |
| 32 to 66 |
| Strength to Weight: Bending, points | 16 to 18 | |
| 27 to 44 |
| Thermal Diffusivity, mm2/s | 29 | |
| 11 |
| Thermal Shock Resistance, points | 14 to 18 | |
| 25 to 53 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.5 | |
| 0 to 0.050 |
| Antimony (Sb), % | 0 to 0.5 | |
| 0 |
| Arsenic (As), % | 0 | |
| 0 to 0.020 |
| Bismuth (Bi), % | 0.5 to 2.0 | |
| 0 |
| Carbon (C), % | 0 | |
| 3.4 to 3.8 |
| Chromium (Cr), % | 0 | |
| 0 to 0.1 |
| Copper (Cu), % | 58 to 62 | |
| 0 to 0.8 |
| Iron (Fe), % | 0 to 0.1 | |
| 89.6 to 94 |
| Lead (Pb), % | 0 to 0.010 | |
| 0 |
| Magnesium (Mg), % | 0 | |
| 0 to 0.040 |
| Manganese (Mn), % | 0 to 0.030 | |
| 0.3 to 0.4 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.3 |
| Nickel (Ni), % | 0 to 1.5 | |
| 0 to 2.0 |
| Phosphorus (P), % | 0 to 0.2 | |
| 0 to 0.040 |
| Selenium (Se), % | 0 to 0.2 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 0.1 | |
| 2.3 to 2.7 |
| Sulfur (S), % | 0 | |
| 0 to 0.020 |
| Tin (Sn), % | 1.0 to 1.8 | |
| 0 to 0.020 |
| Vanadium (V), % | 0 | |
| 0 to 0.1 |
| Zinc (Zn), % | 30.6 to 40.5 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |