C49300 Brass vs. C75700 Nickel Silver
Both C49300 brass and C75700 nickel silver are copper alloys. They have 83% of their average alloy composition in common.
For each property being compared, the top bar is C49300 brass and the bottom bar is C75700 nickel silver.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 120 |
| Elongation at Break, % | 4.5 to 20 | |
| 3.2 to 22 |
| Poisson's Ratio | 0.31 | |
| 0.32 |
| Shear Modulus, GPa | 40 | |
| 45 |
| Shear Strength, MPa | 270 to 290 | |
| 350 to 370 |
| Tensile Strength: Ultimate (UTS), MPa | 430 to 520 | |
| 590 to 610 |
| Tensile Strength: Yield (Proof), MPa | 210 to 410 | |
| 470 to 580 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 200 |
| Maximum Temperature: Mechanical, °C | 120 | |
| 180 |
| Melting Completion (Liquidus), °C | 880 | |
| 1040 |
| Melting Onset (Solidus), °C | 840 | |
| 990 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 390 |
| Thermal Conductivity, W/m-K | 88 | |
| 40 |
| Thermal Expansion, µm/m-K | 20 | |
| 16 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 15 | |
| 8.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 17 | |
| 8.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 26 | |
| 30 |
| Density, g/cm3 | 8.0 | |
| 8.4 |
| Embodied Carbon, kg CO2/kg material | 3.0 | |
| 3.6 |
| Embodied Energy, MJ/kg | 50 | |
| 56 |
| Embodied Water, L/kg | 370 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 21 to 71 | |
| 19 to 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 220 to 800 | |
| 930 to 1410 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.8 |
| Stiffness to Weight: Bending, points | 19 | |
| 19 |
| Strength to Weight: Axial, points | 15 to 18 | |
| 19 to 20 |
| Strength to Weight: Bending, points | 16 to 18 | |
| 19 |
| Thermal Diffusivity, mm2/s | 29 | |
| 12 |
| Thermal Shock Resistance, points | 14 to 18 | |
| 22 to 23 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.5 | |
| 0 |
| Antimony (Sb), % | 0 to 0.5 | |
| 0 |
| Bismuth (Bi), % | 0.5 to 2.0 | |
| 0 |
| Copper (Cu), % | 58 to 62 | |
| 63.5 to 66.5 |
| Iron (Fe), % | 0 to 0.1 | |
| 0 to 0.25 |
| Lead (Pb), % | 0 to 0.010 | |
| 0 to 0.050 |
| Manganese (Mn), % | 0 to 0.030 | |
| 0 to 0.5 |
| Nickel (Ni), % | 0 to 1.5 | |
| 11 to 13 |
| Phosphorus (P), % | 0 to 0.2 | |
| 0 |
| Selenium (Se), % | 0 to 0.2 | |
| 0 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 |
| Tin (Sn), % | 1.0 to 1.8 | |
| 0 |
| Zinc (Zn), % | 30.6 to 40.5 | |
| 19.2 to 25.5 |
| Residuals, % | 0 | |
| 0 to 0.5 |