C49300 Brass vs. N06200 Nickel

C49300 brass belongs to the copper alloys classification, while N06200 nickel belongs to the nickel alloys. There are 29 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is C49300 brass and the bottom bar is N06200 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 100
220
Elongation at Break, % 4.5 to 20
51
Poisson's Ratio 0.31
0.29
Shear Modulus, GPa 40
84
Shear Strength, MPa 270 to 290
560
Tensile Strength: Ultimate (UTS), MPa 430 to 520
780
Tensile Strength: Yield (Proof), MPa 210 to 410
320

Thermal Properties

Latent Heat of Fusion, J/g 170
330
Maximum Temperature: Mechanical, °C 120
990
Melting Completion (Liquidus), °C 880
1500
Melting Onset (Solidus), °C 840
1450
Specific Heat Capacity, J/kg-K 380
430
Thermal Conductivity, W/m-K 88
9.1
Thermal Expansion, µm/m-K 20
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 15
1.3
Electrical Conductivity: Equal Weight (Specific), % IACS 17
1.4

Otherwise Unclassified Properties

Base Metal Price, % relative 26
65
Density, g/cm3 8.0
8.7
Embodied Carbon, kg CO2/kg material 3.0
12
Embodied Energy, MJ/kg 50
160
Embodied Water, L/kg 370
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 21 to 71
320
Resilience: Unit (Modulus of Resilience), kJ/m3 220 to 800
240
Stiffness to Weight: Axial, points 7.2
14
Stiffness to Weight: Bending, points 19
23
Strength to Weight: Axial, points 15 to 18
25
Strength to Weight: Bending, points 16 to 18
22
Thermal Diffusivity, mm2/s 29
2.4
Thermal Shock Resistance, points 14 to 18
21

Alloy Composition

Aluminum (Al), % 0 to 0.5
0 to 0.5
Antimony (Sb), % 0 to 0.5
0
Bismuth (Bi), % 0.5 to 2.0
0
Carbon (C), % 0
0 to 0.010
Chromium (Cr), % 0
22 to 24
Cobalt (Co), % 0
0 to 2.0
Copper (Cu), % 58 to 62
1.3 to 1.9
Iron (Fe), % 0 to 0.1
0 to 3.0
Lead (Pb), % 0 to 0.010
0
Manganese (Mn), % 0 to 0.030
0 to 0.010
Molybdenum (Mo), % 0
15 to 17
Nickel (Ni), % 0 to 1.5
51 to 61.7
Phosphorus (P), % 0 to 0.2
0 to 0.025
Selenium (Se), % 0 to 0.2
0
Silicon (Si), % 0 to 0.1
0 to 0.080
Sulfur (S), % 0
0 to 0.010
Tin (Sn), % 1.0 to 1.8
0
Zinc (Zn), % 30.6 to 40.5
0
Residuals, % 0 to 0.5
0