C51100 Bronze vs. ASTM B780 Alloy

C51100 bronze belongs to the copper alloys classification, while ASTM B780 alloy belongs to the otherwise unclassified metals. They have a modest 25% of their average alloy composition in common, which, by itself, doesn't mean much. There are 17 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is C51100 bronze and the bottom bar is ASTM B780 alloy.

UNS C51100 (CW450K) Phosphor Bronze ASTM B780 Silver-Copper-Nickel Electrical Contact Alloy

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		110
Elastic (Young's, Tensile) Modulus, GPa		83

Elongation at Break, %		2.5 to 50
Elongation at Break, %		1.1 to 9.1

Poisson's Ratio		0.34
Poisson's Ratio		0.36

Shear Modulus, GPa		42
Shear Modulus, GPa		30

Shear Strength, MPa		230 to 410
Shear Strength, MPa		200 to 340

Tensile Strength: Ultimate (UTS), MPa		330 to 720
Tensile Strength: Ultimate (UTS), MPa		330 to 590

Thermal Properties

Latent Heat of Fusion, J/g		200
Latent Heat of Fusion, J/g		140

Specific Heat Capacity, J/kg-K		380
Specific Heat Capacity, J/kg-K		270

Thermal Expansion, µm/m-K		18
Thermal Expansion, µm/m-K		18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS		20
Electrical Conductivity: Equal Volume, % IACS		70 to 76

Electrical Conductivity: Equal Weight (Specific), % IACS		20
Electrical Conductivity: Equal Weight (Specific), % IACS		62 to 68

Otherwise Unclassified Properties

Density, g/cm³		8.9
Density, g/cm³		10

Common Calculations

Stiffness to Weight: Axial, points		7.1
Stiffness to Weight: Axial, points		4.5

Stiffness to Weight: Bending, points		18
Stiffness to Weight: Bending, points		14

Strength to Weight: Axial, points		10 to 22
Strength to Weight: Axial, points		9.1 to 16

Strength to Weight: Bending, points		12 to 20
Strength to Weight: Bending, points		11 to 15

Thermal Shock Resistance, points		12 to 26
Thermal Shock Resistance, points		16 to 29

Alloy Composition

Cadmium (Cd), %		0
Cadmium (Cd), %		0 to 0.050

Copper (Cu), %		93.8 to 96.5
Copper (Cu), %		23.5 to 25.7

Iron (Fe), %		0 to 0.1
Iron (Fe), %		0 to 0.050

Lead (Pb), %		0 to 0.050
Lead (Pb), %		0 to 0.030

Nickel (Ni), %		0
Nickel (Ni), %		0.35 to 0.65

Phosphorus (P), %		0.030 to 0.35
Phosphorus (P), %		0

Silver (Ag), %		0
Silver (Ag), %		74 to 76

Tin (Sn), %		3.5 to 4.9
Tin (Sn), %		0

Zinc (Zn), %		0 to 0.3
Zinc (Zn), %		0 to 0.060

Residuals, %		0 to 0.5
Residuals, %		0