C51900 Bronze vs. AISI 304 Stainless Steel
C51900 bronze belongs to the copper alloys classification, while AISI 304 stainless steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is C51900 bronze and the bottom bar is AISI 304 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 200 |
| Elongation at Break, % | 14 to 29 | |
| 8.0 to 43 |
| Poisson's Ratio | 0.34 | |
| 0.28 |
| Shear Modulus, GPa | 42 | |
| 77 |
| Shear Strength, MPa | 320 to 370 | |
| 400 to 690 |
| Tensile Strength: Ultimate (UTS), MPa | 380 to 620 | |
| 580 to 1180 |
| Tensile Strength: Yield (Proof), MPa | 390 to 570 | |
| 230 to 860 |
Thermal Properties
| Latent Heat of Fusion, J/g | 200 | |
| 290 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 710 |
| Melting Completion (Liquidus), °C | 1040 | |
| 1450 |
| Melting Onset (Solidus), °C | 930 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 480 |
| Thermal Conductivity, W/m-K | 66 | |
| 16 |
| Thermal Expansion, µm/m-K | 18 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 14 | |
| 2.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 14 | |
| 2.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 33 | |
| 15 |
| Density, g/cm3 | 8.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 3.2 | |
| 3.0 |
| Embodied Energy, MJ/kg | 51 | |
| 43 |
| Embodied Water, L/kg | 360 | |
| 150 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 55 to 180 | |
| 86 to 250 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 680 to 1450 | |
| 140 to 1870 |
| Stiffness to Weight: Axial, points | 7.0 | |
| 14 |
| Stiffness to Weight: Bending, points | 18 | |
| 25 |
| Strength to Weight: Axial, points | 12 to 19 | |
| 21 to 42 |
| Strength to Weight: Bending, points | 13 to 18 | |
| 20 to 32 |
| Thermal Diffusivity, mm2/s | 20 | |
| 4.2 |
| Thermal Shock Resistance, points | 14 to 22 | |
| 12 to 25 |
Alloy Composition
| Carbon (C), % | 0 | |
| 0 to 0.080 |
| Chromium (Cr), % | 0 | |
| 18 to 20 |
| Copper (Cu), % | 91.7 to 95 | |
| 0 |
| Iron (Fe), % | 0 to 0.1 | |
| 66.5 to 74 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0 to 2.0 |
| Nickel (Ni), % | 0 | |
| 8.0 to 10.5 |
| Nitrogen (N), % | 0 | |
| 0 to 0.1 |
| Phosphorus (P), % | 0.030 to 0.35 | |
| 0 to 0.045 |
| Silicon (Si), % | 0 | |
| 0 to 0.75 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Tin (Sn), % | 5.0 to 7.0 | |
| 0 |
| Zinc (Zn), % | 0 to 0.3 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |