C51900 Bronze vs. EN 2.4816 Nickel
C51900 bronze belongs to the copper alloys classification, while EN 2.4816 nickel belongs to the nickel alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is C51900 bronze and the bottom bar is EN 2.4816 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 190 |
| Elongation at Break, % | 14 to 29 | |
| 34 |
| Poisson's Ratio | 0.34 | |
| 0.29 |
| Shear Modulus, GPa | 42 | |
| 74 |
| Shear Strength, MPa | 320 to 370 | |
| 470 |
| Tensile Strength: Ultimate (UTS), MPa | 380 to 620 | |
| 700 |
| Tensile Strength: Yield (Proof), MPa | 390 to 570 | |
| 270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 200 | |
| 310 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 1150 |
| Melting Completion (Liquidus), °C | 1040 | |
| 1370 |
| Melting Onset (Solidus), °C | 930 | |
| 1320 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 460 |
| Thermal Conductivity, W/m-K | 66 | |
| 15 |
| Thermal Expansion, µm/m-K | 18 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 14 | |
| 1.7 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 14 | |
| 1.8 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 33 | |
| 55 |
| Density, g/cm3 | 8.8 | |
| 8.5 |
| Embodied Carbon, kg CO2/kg material | 3.2 | |
| 9.0 |
| Embodied Energy, MJ/kg | 51 | |
| 130 |
| Embodied Water, L/kg | 360 | |
| 260 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 55 to 180 | |
| 190 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 680 to 1450 | |
| 190 |
| Stiffness to Weight: Axial, points | 7.0 | |
| 13 |
| Stiffness to Weight: Bending, points | 18 | |
| 23 |
| Strength to Weight: Axial, points | 12 to 19 | |
| 23 |
| Strength to Weight: Bending, points | 13 to 18 | |
| 21 |
| Thermal Diffusivity, mm2/s | 20 | |
| 3.8 |
| Thermal Shock Resistance, points | 14 to 22 | |
| 20 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.3 |
| Carbon (C), % | 0 | |
| 0.050 to 0.1 |
| Chromium (Cr), % | 0 | |
| 14 to 17 |
| Copper (Cu), % | 91.7 to 95 | |
| 0 to 0.5 |
| Iron (Fe), % | 0 to 0.1 | |
| 6.0 to 10 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0 to 1.0 |
| Nickel (Ni), % | 0 | |
| 72 to 80 |
| Phosphorus (P), % | 0.030 to 0.35 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 | |
| 0 to 0.015 |
| Tin (Sn), % | 5.0 to 7.0 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 0 to 0.3 |
| Zinc (Zn), % | 0 to 0.3 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |