C53800 Bronze vs. SAE-AISI 50B60 Steel
C53800 bronze belongs to the copper alloys classification, while SAE-AISI 50B60 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is C53800 bronze and the bottom bar is SAE-AISI 50B60 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 190 |
| Elongation at Break, % | 2.3 | |
| 12 to 20 |
| Poisson's Ratio | 0.34 | |
| 0.29 |
| Shear Modulus, GPa | 40 | |
| 72 |
| Shear Strength, MPa | 470 | |
| 380 |
| Tensile Strength: Ultimate (UTS), MPa | 830 | |
| 610 to 630 |
| Tensile Strength: Yield (Proof), MPa | 660 | |
| 350 to 530 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 160 | |
| 410 |
| Melting Completion (Liquidus), °C | 980 | |
| 1450 |
| Melting Onset (Solidus), °C | 800 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 360 | |
| 470 |
| Thermal Conductivity, W/m-K | 61 | |
| 45 |
| Thermal Expansion, µm/m-K | 18 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 9.0 | |
| 7.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 9.3 | |
| 8.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 37 | |
| 2.0 |
| Density, g/cm3 | 8.7 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 3.9 | |
| 1.4 |
| Embodied Energy, MJ/kg | 64 | |
| 19 |
| Embodied Water, L/kg | 420 | |
| 48 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 18 | |
| 71 to 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2020 | |
| 330 to 750 |
| Stiffness to Weight: Axial, points | 6.8 | |
| 13 |
| Stiffness to Weight: Bending, points | 18 | |
| 24 |
| Strength to Weight: Axial, points | 26 | |
| 22 to 23 |
| Strength to Weight: Bending, points | 22 | |
| 20 to 21 |
| Thermal Diffusivity, mm2/s | 19 | |
| 12 |
| Thermal Shock Resistance, points | 31 | |
| 20 |
Alloy Composition
| Boron (B), % | 0 | |
| 0.00050 to 0.0030 |
| Carbon (C), % | 0 | |
| 0.56 to 0.64 |
| Chromium (Cr), % | 0 | |
| 0.4 to 0.6 |
| Copper (Cu), % | 85.1 to 86.5 | |
| 0 |
| Iron (Fe), % | 0 to 0.030 | |
| 97.3 to 98.1 |
| Lead (Pb), % | 0.4 to 0.6 | |
| 0 |
| Manganese (Mn), % | 0 to 0.060 | |
| 0.75 to 1.0 |
| Nickel (Ni), % | 0 to 0.030 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.035 |
| Silicon (Si), % | 0 | |
| 0.15 to 0.35 |
| Sulfur (S), % | 0 | |
| 0 to 0.040 |
| Tin (Sn), % | 13.1 to 13.9 | |
| 0 |
| Zinc (Zn), % | 0 to 0.12 | |
| 0 |
| Residuals, % | 0 to 0.2 | |
| 0 |