C55181 Copper vs. SAE-AISI H24 Steel
C55181 copper belongs to the copper alloys classification, while SAE-AISI H24 steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is C55181 copper and the bottom bar is SAE-AISI H24 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 200 |
| Poisson's Ratio | 0.34 | |
| 0.29 |
| Shear Modulus, GPa | 40 | |
| 78 |
| Tensile Strength: Ultimate (UTS), MPa | 200 | |
| 720 to 1990 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 240 |
| Melting Completion (Liquidus), °C | 790 | |
| 1750 |
| Melting Onset (Solidus), °C | 710 | |
| 1700 |
| Specific Heat Capacity, J/kg-K | 410 | |
| 420 |
| Thermal Expansion, µm/m-K | 16 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 28 | |
| 37 |
| Density, g/cm3 | 8.5 | |
| 9.1 |
| Embodied Carbon, kg CO2/kg material | 2.4 | |
| 6.1 |
| Embodied Energy, MJ/kg | 38 | |
| 93 |
| Embodied Water, L/kg | 290 | |
| 78 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.0 | |
| 12 |
| Stiffness to Weight: Bending, points | 19 | |
| 22 |
| Strength to Weight: Axial, points | 6.5 | |
| 22 to 61 |
| Strength to Weight: Bending, points | 8.9 | |
| 20 to 39 |
| Thermal Shock Resistance, points | 8.2 | |
| 22 to 61 |
Alloy Composition
| Carbon (C), % | 0 | |
| 0.42 to 0.53 |
| Chromium (Cr), % | 0 | |
| 2.5 to 3.5 |
| Copper (Cu), % | 92.4 to 93 | |
| 0 to 0.25 |
| Iron (Fe), % | 0 | |
| 78 to 82.4 |
| Manganese (Mn), % | 0 | |
| 0.15 to 0.4 |
| Nickel (Ni), % | 0 | |
| 0 to 0.3 |
| Phosphorus (P), % | 7.0 to 7.5 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 | |
| 0.15 to 0.4 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Tungsten (W), % | 0 | |
| 14 to 16 |
| Vanadium (V), % | 0 | |
| 0.4 to 0.6 |
| Residuals, % | 0 to 0.15 | |
| 0 |