C55280 Copper vs. Grade 8 Babbitt Metal
C55280 copper belongs to the copper alloys classification, while grade 8 Babbitt Metal belongs to the otherwise unclassified metals. There are 13 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is C55280 copper and the bottom bar is grade 8 Babbitt Metal.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 24 |
| Poisson's Ratio | 0.34 | |
| 0.41 |
| Shear Modulus, GPa | 40 | |
| 8.5 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 46 |
| Melting Completion (Liquidus), °C | 790 | |
| 270 |
| Melting Onset (Solidus), °C | 640 | |
| 240 |
| Specific Heat Capacity, J/kg-K | 410 | |
| 150 |
| Thermal Expansion, µm/m-K | 16 | |
| 24 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.5 | |
| 10 |
| Embodied Carbon, kg CO2/kg material | 4.2 | |
| 3.9 |
| Embodied Energy, MJ/kg | 67 | |
| 53 |
Common Calculations
| Stiffness to Weight: Axial, points | 6.9 | |
| 1.3 |
| Stiffness to Weight: Bending, points | 19 | |
| 9.2 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.0050 |
| Antimony (Sb), % | 0 | |
| 14 to 16 |
| Arsenic (As), % | 0 | |
| 0.3 to 0.6 |
| Bismuth (Bi), % | 0 | |
| 0 to 0.1 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.050 |
| Copper (Cu), % | 90.5 to 91.4 | |
| 0 to 0.5 |
| Iron (Fe), % | 0 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 | |
| 77.1 to 81.2 |
| Phosphorus (P), % | 6.8 to 7.2 | |
| 0 |
| Silver (Ag), % | 1.8 to 2.2 | |
| 0 |
| Tin (Sn), % | 0 | |
| 4.5 to 5.5 |
| Zinc (Zn), % | 0 | |
| 0 to 0.0050 |
| Residuals, % | 0 to 0.15 | |
| 0 |