C55280 Copper vs. Monel K-500
C55280 copper belongs to the copper alloys classification, while Monel K-500 belongs to the nickel alloys. They have a modest 30% of their average alloy composition in common, which, by itself, doesn't mean much. There are 18 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.
For each property being compared, the top bar is C55280 copper and the bottom bar is Monel K-500.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 160 |
| Poisson's Ratio | 0.34 | |
| 0.32 |
| Shear Modulus, GPa | 40 | |
| 61 |
| Tensile Strength: Ultimate (UTS), MPa | 180 | |
| 640 to 1100 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 270 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 900 |
| Melting Completion (Liquidus), °C | 790 | |
| 1350 |
| Melting Onset (Solidus), °C | 640 | |
| 1320 |
| Specific Heat Capacity, J/kg-K | 410 | |
| 440 |
| Thermal Expansion, µm/m-K | 16 | |
| 14 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.5 | |
| 8.7 |
| Embodied Carbon, kg CO2/kg material | 4.2 | |
| 8.1 |
| Embodied Energy, MJ/kg | 67 | |
| 120 |
Common Calculations
| Stiffness to Weight: Axial, points | 6.9 | |
| 10 |
| Stiffness to Weight: Bending, points | 19 | |
| 21 |
| Strength to Weight: Axial, points | 5.9 | |
| 21 to 35 |
| Strength to Weight: Bending, points | 8.3 | |
| 19 to 27 |
| Thermal Shock Resistance, points | 7.4 | |
| 21 to 36 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 2.3 to 3.2 |
| Carbon (C), % | 0 | |
| 0 to 0.18 |
| Copper (Cu), % | 90.5 to 91.4 | |
| 27 to 33 |
| Iron (Fe), % | 0 | |
| 0 to 2.0 |
| Manganese (Mn), % | 0 | |
| 0 to 1.5 |
| Nickel (Ni), % | 0 | |
| 63 to 70.4 |
| Phosphorus (P), % | 6.8 to 7.2 | |
| 0 |
| Silicon (Si), % | 0 | |
| 0 to 0.5 |
| Silver (Ag), % | 1.8 to 2.2 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.010 |
| Titanium (Ti), % | 0 | |
| 0.35 to 0.85 |
| Residuals, % | 0 to 0.15 | |
| 0 |