C55280 Copper vs. SAE-AISI H43 Steel
C55280 copper belongs to the copper alloys classification, while SAE-AISI H43 steel belongs to the iron alloys. There are 17 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is C55280 copper and the bottom bar is SAE-AISI H43 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 200 |
| Poisson's Ratio | 0.34 | |
| 0.29 |
| Shear Modulus, GPa | 40 | |
| 77 |
| Tensile Strength: Ultimate (UTS), MPa | 180 | |
| 710 to 2140 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 270 |
| Melting Completion (Liquidus), °C | 790 | |
| 1530 |
| Melting Onset (Solidus), °C | 640 | |
| 1480 |
| Specific Heat Capacity, J/kg-K | 410 | |
| 460 |
| Thermal Expansion, µm/m-K | 16 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.5 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 4.2 | |
| 8.2 |
| Embodied Energy, MJ/kg | 67 | |
| 120 |
Common Calculations
| Stiffness to Weight: Axial, points | 6.9 | |
| 14 |
| Stiffness to Weight: Bending, points | 19 | |
| 24 |
| Strength to Weight: Axial, points | 5.9 | |
| 25 to 75 |
| Strength to Weight: Bending, points | 8.3 | |
| 22 to 46 |
| Thermal Shock Resistance, points | 7.4 | |
| 21 to 62 |
Alloy Composition
| Carbon (C), % | 0 | |
| 0.5 to 0.65 |
| Chromium (Cr), % | 0 | |
| 3.8 to 4.5 |
| Copper (Cu), % | 90.5 to 91.4 | |
| 0 |
| Iron (Fe), % | 0 | |
| 83.2 to 85.9 |
| Manganese (Mn), % | 0 | |
| 0.15 to 0.4 |
| Molybdenum (Mo), % | 0 | |
| 7.8 to 8.5 |
| Phosphorus (P), % | 6.8 to 7.2 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 | |
| 0.2 to 0.45 |
| Silver (Ag), % | 1.8 to 2.2 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Vanadium (V), % | 0 | |
| 1.8 to 2.2 |
| Residuals, % | 0 to 0.15 | |
| 0 |