C55280 Copper vs. Type 4 Magnetic Alloy
C55280 copper belongs to the copper alloys classification, while Type 4 magnetic alloy belongs to the nickel alloys. There are 18 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is C55280 copper and the bottom bar is Type 4 magnetic alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 190 |
| Poisson's Ratio | 0.34 | |
| 0.31 |
| Shear Modulus, GPa | 40 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 180 | |
| 620 to 1100 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 290 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 900 |
| Melting Completion (Liquidus), °C | 790 | |
| 1420 |
| Melting Onset (Solidus), °C | 640 | |
| 1370 |
| Specific Heat Capacity, J/kg-K | 410 | |
| 440 |
| Thermal Expansion, µm/m-K | 16 | |
| 11 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.5 | |
| 8.8 |
| Embodied Carbon, kg CO2/kg material | 4.2 | |
| 10 |
| Embodied Energy, MJ/kg | 67 | |
| 140 |
Common Calculations
| Stiffness to Weight: Axial, points | 6.9 | |
| 12 |
| Stiffness to Weight: Bending, points | 19 | |
| 22 |
| Strength to Weight: Axial, points | 5.9 | |
| 19 to 35 |
| Strength to Weight: Bending, points | 8.3 | |
| 18 to 27 |
| Thermal Shock Resistance, points | 7.4 | |
| 21 to 37 |
Alloy Composition
| Carbon (C), % | 0 | |
| 0 to 0.050 |
| Chromium (Cr), % | 0 | |
| 0 to 0.3 |
| Cobalt (Co), % | 0 | |
| 0 to 0.5 |
| Copper (Cu), % | 90.5 to 91.4 | |
| 0 to 0.3 |
| Iron (Fe), % | 0 | |
| 9.5 to 17.5 |
| Manganese (Mn), % | 0 | |
| 0 to 0.8 |
| Molybdenum (Mo), % | 0 | |
| 3.5 to 6.0 |
| Nickel (Ni), % | 0 | |
| 79 to 82 |
| Phosphorus (P), % | 6.8 to 7.2 | |
| 0 to 0.010 |
| Silicon (Si), % | 0 | |
| 0 to 0.5 |
| Silver (Ag), % | 1.8 to 2.2 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.020 |
| Residuals, % | 0 to 0.15 | |
| 0 |