C55280 Copper vs. C16500 Copper
Both C55280 copper and C16500 copper are copper alloys. They have a moderately high 91% of their average alloy composition in common. There are 18 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is C55280 copper and the bottom bar is C16500 copper.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 110 | |
110 |
Poisson's Ratio | 0.34 | |
0.34 |
Shear Modulus, GPa | 40 | |
43 |
Tensile Strength: Ultimate (UTS), MPa | 180 | |
280 to 530 |
Thermal Properties
Latent Heat of Fusion, J/g | 190 | |
210 |
Maximum Temperature: Mechanical, °C | 200 | |
340 |
Melting Completion (Liquidus), °C | 790 | |
1070 |
Melting Onset (Solidus), °C | 640 | |
1010 |
Specific Heat Capacity, J/kg-K | 410 | |
380 |
Thermal Expansion, µm/m-K | 16 | |
17 |
Otherwise Unclassified Properties
Density, g/cm3 | 8.5 | |
8.9 |
Embodied Carbon, kg CO2/kg material | 4.2 | |
2.6 |
Embodied Energy, MJ/kg | 67 | |
42 |
Common Calculations
Stiffness to Weight: Axial, points | 6.9 | |
7.1 |
Stiffness to Weight: Bending, points | 19 | |
18 |
Strength to Weight: Axial, points | 5.9 | |
8.6 to 17 |
Strength to Weight: Bending, points | 8.3 | |
11 to 16 |
Thermal Shock Resistance, points | 7.4 | |
9.8 to 19 |
Alloy Composition
Cadmium (Cd), % | 0 | |
0.6 to 1.0 |
Copper (Cu), % | 90.5 to 91.4 | |
97.8 to 98.9 |
Iron (Fe), % | 0 | |
0 to 0.020 |
Phosphorus (P), % | 6.8 to 7.2 | |
0 |
Silver (Ag), % | 1.8 to 2.2 | |
0 |
Tin (Sn), % | 0 | |
0.5 to 0.7 |
Residuals, % | 0 | |
0 to 0.5 |