C55280 Copper vs. C55282 Copper
Both C55280 copper and C55282 copper are copper alloys. Both are furnished in the as-fabricated (no temper or treatment) condition. They have a very high 97% of their average alloy composition in common.
For each property being compared, the top bar is C55280 copper and the bottom bar is C55282 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 110 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Shear Modulus, GPa | 40 | |
| 39 |
| Tensile Strength: Ultimate (UTS), MPa | 180 | |
| 180 |
Thermal Properties
| Brazing Temperature, °C | 730 to 820 | |
| 700 to 820 |
| Latent Heat of Fusion, J/g | 190 | |
| 190 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 200 |
| Melting Completion (Liquidus), °C | 790 | |
| 770 |
| Melting Onset (Solidus), °C | 640 | |
| 640 |
| Specific Heat Capacity, J/kg-K | 410 | |
| 400 |
| Thermal Expansion, µm/m-K | 16 | |
| 16 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.5 | |
| 8.6 |
| Embodied Carbon, kg CO2/kg material | 4.2 | |
| 7.0 |
| Embodied Energy, MJ/kg | 67 | |
| 110 |
Common Calculations
| Stiffness to Weight: Axial, points | 6.9 | |
| 6.8 |
| Stiffness to Weight: Bending, points | 19 | |
| 18 |
| Strength to Weight: Axial, points | 5.9 | |
| 5.8 |
| Strength to Weight: Bending, points | 8.3 | |
| 8.2 |
| Thermal Shock Resistance, points | 7.4 | |
| 7.4 |
Alloy Composition
| Copper (Cu), % | 90.5 to 91.4 | |
| 87.7 to 88.7 |
| Phosphorus (P), % | 6.8 to 7.2 | |
| 6.5 to 7.0 |
| Silver (Ag), % | 1.8 to 2.2 | |
| 4.8 to 5.2 |
| Residuals, % | 0 | |
| 0 to 0.15 |