C55281 Copper vs. C61500 Bronze
Both C55281 copper and C61500 bronze are copper alloys. They have 89% of their average alloy composition in common. There are 18 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is C55281 copper and the bottom bar is C61500 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 110 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Shear Modulus, GPa | 40 | |
| 42 |
| Tensile Strength: Ultimate (UTS), MPa | 190 | |
| 480 to 970 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 220 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 220 |
| Melting Completion (Liquidus), °C | 810 | |
| 1040 |
| Melting Onset (Solidus), °C | 640 | |
| 1030 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 430 |
| Thermal Expansion, µm/m-K | 16 | |
| 18 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.7 | |
| 8.4 |
| Embodied Carbon, kg CO2/kg material | 7.0 | |
| 3.2 |
| Embodied Energy, MJ/kg | 110 | |
| 52 |
Common Calculations
| Stiffness to Weight: Axial, points | 6.9 | |
| 7.5 |
| Stiffness to Weight: Bending, points | 18 | |
| 19 |
| Strength to Weight: Axial, points | 6.1 | |
| 16 to 32 |
| Strength to Weight: Bending, points | 8.5 | |
| 16 to 26 |
| Thermal Shock Resistance, points | 7.7 | |
| 17 to 34 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 7.7 to 8.3 |
| Copper (Cu), % | 88.5 to 89.4 | |
| 89 to 90.5 |
| Lead (Pb), % | 0 | |
| 0 to 0.015 |
| Nickel (Ni), % | 0 | |
| 1.8 to 2.2 |
| Phosphorus (P), % | 5.8 to 6.2 | |
| 0 |
| Silver (Ag), % | 4.8 to 5.2 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.5 |